Study on preparation of vaterite from dolomite by ammonia-alkali method and its mechanism
Received date: 2020-08-11
Online published: 2021-05-12
Calcium carbonate with high content of vaterite was prepared by imitating Solvay ammonia-alkali method with dolomite as starting material in alkaline environment.The results of XRD and SEM showed that the product with carbonization temperature of 20~40 ℃ was vaterite,40~60 ℃ was calcite and 60~90 ℃ was aragonite.The high magnification SEM of vaterite showed that the product had many microporous structures.The specific surface area of the product was determined to be 32.653 m2/g and the pore size was 2.972 nm.It provides a good space for the loading of biomolecules.The analysis of the formation mechanism of vaterite showed that the NH4+-NH3 buffer system could not only increase the supersaturation of calcium carbonate in the solution,but also improve the solution environment and provide a good solution environment for the growth of vaterite.The trace amount of Mg2+ in the solution played a role in promoting the formation of intact crystal forms.
Key words: dolomite; buffer system; vaterite; calcium carbonate
Tianbo Fan , Xiaohui Jia , Dongxue Han , Si Chen , Yu Jiang , Tingting Hu , Hongfan Guo , Li Li , Yunyi Liu . Study on preparation of vaterite from dolomite by ammonia-alkali method and its mechanism[J]. Inorganic Chemicals Industry, 2021 , 53(5) : 56 -60 . DOI: 10.11962/1006-4990.2020-0339
[1] | 罗佳. 球霰石碳酸钙的仿生合成及其药物载体研究[D]. 上海:华东理工大学, 2016. |
[2] | Nishiyama R, Munemoto T, Fukushi K. Formation condition of mo-nohydrocalcite from CaCl2-MgCl2-Na2CO3 solutions[J]. Geochimica at Cosmochimica Acta, 2013,100:217-231. |
[3] | Zou Z Y, Habraken W J E M, Matveeva G, et al. A hydrated crysta-lline calcium carbonate phase:Calcium carbonate hemihydrate[J]. Science, 2019,363(6425):396-400 |
[4] | Volodkin Dmitry. CaCO templated micro-beads and-capsules for bioapplications[J]. Advances in Colloid and Interface Science, 2014,207:306-324. |
[5] | Chen Y, Ji X, Wang X. Microwave-assisted synjournal of spheroidal vaterite CaCO3 in ethylene glycol-water mixed solvents without sur-factants[J]. Journal of Crystal Growth, 2010,312(21):3191-3197. |
[6] | Fu Lianhua, Qi Chao, Hu Yanru, et al. Cellulose/vaterite nanocom-posites:Sonochemical synjournal,characterization,and their appli-cation in protein adsorption[J]. Materials Science & Engineering C, 2019,96:426-435. |
[7] | Wang Xiaoqiang, Wu Congmeng, Tao Kai, et al. Influence of oval-bumin on CaCO3 precipitation during in vitro biomineralization[J]. Journal of Physical Chemistry B, 2010,114(16):5301. |
[8] | Liu Y, Cui Y J, Mao H Y, et al. Calcium carbonate crystallization in the presence of casein[J]. Crystal Growth & Design, 2012,12(10):4720-4726. |
[9] | Porter A L, Wilson W J. Manufacture of precipitated calcium carbona-te of improved color and stable crystalline form:US,6132696A[P]. 2000-10-17. |
[10] | 黄文艺, 马蓝宇, 程昊, 等. 氯化铝对碳酸钙结晶形貌的影响[J]. 无机盐工业, 2018,50(1):20-23. |
[11] | Di Profio Gianluca, Salehi Shabnam Majidi, Caliandro Rocco, et al. Bioinspired synjournal of CaCO3 superstructures through a novel hy-drogel composite membranes mineralization platform:A comprehe-nsive view[J]. Advanced Materials, 2016,28(4):610-616. |
[12] | 郑天文, 陈雪梅. 球霰石碳酸钙微球的合成及其机理[J]. 材料科学与工程学报, 2018(3):358-364 |
[13] | Lo?c Dupont, Fran?ois Portemer, the late Michel Figlarz. Synjournal and study of a well crystallized CaCO3 vaterite showing a new habi-tus[J]. Journal of Materials Chemistry, 1997,7(5):797-800. |
[14] | Dmitry V V, Alexander I P, Michelle P, et al. Matrix polyelectrolyte microcapsules:New system for macromoleculeen-capsulation[J]. Langmuir, 2004,20(8):3398-3406. |
[15] | 陈佩圆, 胡秀平, 孙龙, 等. 快速沉淀法制备高分散高纯度球霰石晶体[J]. 人工晶体学报, 2019,48(3):114-118. |
[16] | Ramesh T N, Inchara S A, Pallavi K. Para-amino benzoic acid-me-diated synjournal of vaterite phase of calcium carbonate[J]. Journal of Chemical Sciences, 2015,127(5):843-848. |
[17] | 邹俭鹏, 杨洪志, 肖平, 等. 微纳分级结构碳酸钙中空微球的可控制备[J]. 无机材料学报, 2016,31(7):711-718. |
[18] | Hu Qiaona, Zhang Jiaming, Henry Teng, et al. Growth process and crystallographic properties of ammonia-induced vaterite[J]. Ame-rican Mineralogist, 2015,97(8/9):1437-1445. |
/
〈 |
|
〉 |