Research on milling and leaching process of manganese in electrolytic manganese slag
Received date: 2020-08-19
Online published: 2021-02-06
In order to promote the comprehensive utilization of electrolytic manganese slag and reduce the waste of manganese resources,using electrolytic manganese slag as raw material,the influence of milling and leaching process conditions on the leaching efficiency of manganese element was researched.The methods of XRD,SEM,XRF and AAS were used to test and analyze the phase,composition and manganese content of manganese slag samples.Results showed that the content of fine particles and the content of manganese in the fine particles were obviously increased via the secondary milling process of manganese slag.Due to the increase of fineness and surface area,the reaction speed of acid leaching of manganese mineral particles in manganese slag was accelerated and the leaching rate was increased.The leaching rate of manganese was obviously affected by time and temperature,but the influence of temperature was more important.The suitable temperature of leaching reaction should be in the range of 70~85 ℃.The leaching rate of manganese was 97.15% when the reaction tempera-ture was 85 ℃ and the time was 1 h.
Key words: electrolytic manganese slag; manganese element; milling; leaching
Tao Li , Guohua Ma . Research on milling and leaching process of manganese in electrolytic manganese slag[J]. Inorganic Chemicals Industry, 2021 , 53(2) : 66 -70 . DOI: 10.11962/1006-4990.2020-0172
[1] | He B B, Hu B, Yen H W, et al. High dislocation density-induced large ductility in deformed and partitioned steels[J]. Science, 2017,357(6355):1029-1032. |
[2] | 常军, 贾福康, 胡成山, 等. 电解锰渣基沸石对锰离子的吸附性能研究[J]. 无机盐工业, 2019,51(9):61-65. |
[3] | 吴霜, 王家伟, 刘利, 等. 电解锰渣综合利用评述[J]. 无机盐工业, 2016,48(4):22-25. |
[4] | 周宏研, 陈平, 赵艳荣, 等. 电解锰渣对热焖钢渣活性的硫酸盐激发[J]. 无机盐工业, 2019,51(5):66-69. |
[5] | Chousidis N, Ioannou I, Batis G. Utilization of electrolytic mangane-se dioxide(EMD) waste in concrete exposed to salt crystalliza-tion[J]. Construction and Building Materials, 2018,158:708-718. |
[6] | 冉岚, 刘少友, 文正康. 电解锰渣-废玻璃低温烧结制备陶瓷砖的研究[J]. 无机盐工业, 2014,46(7):56-58. |
[7] | 叶芬, 成昊, 徐丽, 等. 利用电解锰渣制备轻质多孔陶瓷块状材料的研究[J]. 无机盐工业, 2018,50(10):62-65. |
[8] | 符磊, 满瑞林, 扶强, 等. 电解锰阳极泥制备锰酸锂[J]. 广州化工, 2018,45(8):13-15. |
[9] | 谢超, 徐龙君, 李礼. 电解锰渣制备SiO2掺杂锰锌铁氧体[J]. 人工晶体学报, 2012,41(3):816-820. |
[10] | 陆建平, 马柳军, 黄彦明, 等. 聚环氧琥珀酸对锰渣中锰的萃取研究[J]. 环境科学与技术, 2011,34(8):101-103. |
[11] | 范丹, 邓倩, 熊利芝, 等. 从电解锰渣中提取金属锰[J]. 吉首大学学报:自然科学版, 2012,33(1):94-97. |
[12] | 黄华军, 李小明, 曹建兵, 等. 优势菌种浸取电解锰渣中锰的影响因素研究[J]. 环境工程学报, 2011,5(9):2120-2124. |
[13] | 杨晓红, 向欣, 薛希仕. 电解锰渣酸浸实验条件探究[J]. 硅酸盐通报, 2018,37(7):2326-2330. |
/
〈 |
|
〉 |