Synthesis of aggregated nano-sized ZSM-5 zeolite with ternary pore structure

  • Xiaoguo Li ,
  • Xiaotong Mi ,
  • Zhanggui Hou
Expand
  • CNOOC Research Institute of Refining and Petrochemicals,Beijing 102200,China

Received date: 2020-06-15

  Online published: 2020-12-15

Abstract

A series of ZSM-5 zeolite were hydrothermally synthesized by using the double template system of n-butylamine and ZSM-5 crystal seed.The influence of content of seed and n-butylamine,and crystallication process on the physicochemical properties,pore structure and morphology of obtained zeolites were investigated.The obtained zeolites were subjected to X-ray diffraction(XRD),N2 adsorption-desorption and scanning electron microscopy(SEM) characterization analysis.The analysis results showed that the obtained material was aggregated nano-sized ZSM-5 zeolite with ternary pore structure,and n-butylamine and seed crystals had a synergistic effect in the synthesis process.Under the synthesis conditions of n(n-butyla-mine)/n(SiO2)=0.26,seed addition amount of 3%(mass fraction) and crystallization at 120 ℃ for 24 h and then at 170 ℃ for 48 h,the specific surface area and external surface area were 364 m2/g and 59 m2/g,respectively.

Cite this article

Xiaoguo Li , Xiaotong Mi , Zhanggui Hou . Synthesis of aggregated nano-sized ZSM-5 zeolite with ternary pore structure[J]. Inorganic Chemicals Industry, 2020 , 52(12) : 104 -108 . DOI: 10.11962/1006-4990.2020-0235

References

[1] Wen C, Wang C, Chen L, et al. Effect of hierarchical ZSM-5 zeolite support on direct transformation from syngas to aromatics over the iron-based catalyst[J]. Fuel, 2019,244:492-498.
[2] Chen H. Aggregates of superfine ZSM-5 crystals:The effect of NaOH on the catalytic performance of methanol to propylene reaction[J]. Microporous and Mesoporous Materials, 2017,244:301-309.
[3] Pan F. A fast route for synthesizing nano-sized ZSM-5 aggregates[J]. Journal of Materials and Chemistry, 2014,2(48):20667-20675.
[4] Hamidzadeh M, Komeili S, Saeidi M. Seed-induced synjournal of ZSM-5 aggregates using the Silicate-1 as a seed:characterization and effect of the Silicate-1 composition[J]. Microporous and Mesoporous Materials, 2018,268:153-161.
[5] Lestari A, Ginting S B, Saputra H. Effect of seed amounts on the synjournal of zeolite ZSM-5 using coal bottom ash and rice husk as sources of silica and alumina by using seeding method[J]. Materials Science Forum, 2019,948:9-13.
[6] Majid H N, Sarah C L. Insight into seed-assisted template free synjournal of ZSM-5 zeolites[J]. Microporous and Mesoporous Materials, 2018,239:444-452.
[7] Gao Y, Zheng B, Wu G, et al. Effect of the Si/Al ratio on the performance of hierarchical ZSM-5 zeolites for methanol aromatization[J]. RSC Advances, 2016,6(87):83581-83588.
[8] Wu Z. Synjournal and consequence of aggregated nanosized ZSM-5 zeolite crystals for methanol to propylene reaction[J]. Industrial &Engineering Chemistry Research, 2019,58:10737-10749.
[9] Zhang L. F-assisted synjournal of a hierarchical ZSM-5 zeolite for methanol to propylene reaction:a b-oriented thinner dimensional morphology[J]. RSC Advances, 2015,5(75):61354-61363.
[10] Xue T, Li S, Wu H H, et al. Eco-friendly and cost-effective synjournal of ZSM-5 aggregates with hierarchical porosity[J]. Industrial & Engineering Chemistry Research, 2017,56:13535-13542.
[11] Shen K, Wangz N, Chen X, et al. Seed-induced and additive-free synjournal of oriented nanorod-assembled meso/macroporous zeolites:Toward efficient and cost-effective catalysts for the MTA reaction[J]. Catalysis Science & Technology, 2017,7(21):5143-5153.
Outlines

/