Preparation and photocatalytic property of MoO3/g-C3N4 composite

  • Nan Yin ,
  • Chanlu Liu ,
  • Jin Zhang
Expand
  • School of Environmental Science,Nanjing Xiaozhuang University,Nanjing 211171,China

Received date: 2020-04-26

  Online published: 2020-11-24

Abstract

Using melamine and ammonium molybdate tetrahydrate as precursors,a novel MoO3/g-C3N4 composite photocatalyst was prepared by hydrothermal method.The samples were characterized by X-ray diffraction(XRD),infrared spectroscopy (FT-IR),scanning electron microscopy(SEM),X-ray photoelectron spectroscopy(XPS) and ultraviolet-visible diffuse reflectometer(DRS).Characterization results showed that the optical absorption of the composites was enhanced when the rodlike MoO3 was loaded on the layered g-C3N4 surface.The experiment of photocatalytic degradation of methylene blue(MB) solution by material visible light showed that the heterojunction produced by MoO3 and g-C3N4 had better absorption light intensity and catalytic degradation performance,especially the 5%(mass fraction) MoO3/g-C3N4 composite photocatalytic degradation rate was the best,reaching 95.7%,higher than that of pure MoO3 and g-C3N4.Free radical and hole trapping experiments show that ·O2- was the main substance in photocatalytic reaction.The MoO3/g-C3N4 composite exhibited excellent stability in four reaction cycles.

Cite this article

Nan Yin , Chanlu Liu , Jin Zhang . Preparation and photocatalytic property of MoO3/g-C3N4 composite[J]. Inorganic Chemicals Industry, 2020 , 52(10) : 161 -165 . DOI: 10.11962/1006-4990.2019-0568

References

[1] Mamba G, Mishra A K. Graphitic carbon nitride(g-C3N4) nanocomposites:A new and exciting generation of visible light driven photocatalysts for environmental pollution remediation[J]. Applied Catalysis B:Environmental, 2016,198:347-377.
[2] 任斌. C3N4/TiO2纳米复合材料的制备及其光催化降解橙黄Ⅱ染料废水的研究[D]. 咸阳:西北农林科技大学, 2018.
[3] 刘亮. 少层氮化碳的制备及其复合材料的光催化性能研究[D]. 镇江:江苏大学, 2017.
[4] 田琪. 氮化碳基异质结的制备及其光催化性能研究[D]. 上海:东华大学, 2018.
[5] 甄延忠, 王杰, 付梦溪, 等. AgI/h-MoO3异质结的构筑及其模拟燃油光催化氧化脱硫活性[J]. 无机化学学报, 2017,33(10):1731-1740.
[6] 刘琴秀. 钼基半导体及其复合物的液相合成与性能研究[D]. 长沙:湖南大学, 2018.
[7] Ahmed S E, Hani N A, Yuan Y Y, et al. Facile water-based strategy for synthesizing MoO3-x nanosheets:efficient visible light photocatalysts for dye degradation[J]. ACS Omega, 2018,3(2):2193-2201.
[8] 马令娟, 侯梦宁, 马宏彬, 等. MoO3-C3N4复合光催化剂的可见光下高效催化降解甲基橙[J]. 无机化学学报, 2018,34(10):1899-1909.
[9] Zhang Xiaoni, Yi Jianjian, Chen Hanxiang, et al. Construction of a few-layer g-C3N4/α-MoO3 nanoneedles all-solid-state Z-scheme photocatalytic system for photocatalytic degradation[J]. Journal of Energy Chemistry, 2019,28(2):65-71.
[10] 王戈. 低温液相法制备纳米三氧化钼的研究[D]. 西安:西安建筑科技大学, 2013.
[11] 张晶, 董玉明, 刘湘, 等. Z型光催化剂Sb2WO6/g-C3N4的制备及光催化性能[J]. 高等学校化学学报, 2019,40(1):123-129.
[12] 邓军阳, 汪杰, 朱思龙, 等. Ag3PO4/Ag2S/g-C3N4复合光催化剂的制备与性能[J]. 无机化学学报, 2019,35(6):955-964.
[13] 董曼茹, 余欣佳, 余健, 等. g-C3N4/ZnO复合材料的制备及其光催化性能分析[J]. 人工晶体学报, 2019,48(7):1314-1319.
[14] 张杰, 蔡天凤, 李会鹏, 等. 磷钨酸掺杂高比表面积g-C3N4催化剂的制备及其光催化性能[J]. 人工晶体学报, 2019,48(1):101-108.
[15] 张丽红. MoO3,SnO(2-x)和Zn2SnO4修饰的g-C3N4催化剂光催化降解染料的研究[D]. 金华:浙江师范大学, 2015.
[16] Fatemeh Darkhosh, Maryam Lashanizadegan, Ali Reza Mahjou, et al. One pot synjournal of CuFeO2@expanding perlite as a novel efficient floating catalyst for rapid degradation of methylene blue under visible light illumination[J]. Solid State Sciences, 2019,91(5):61-72.
Outlines

/