The study of double oxalate lithium borate preparation technology by aqueous phase method
Received date: 2020-04-29
Online published: 2020-11-24
The double oxalate lithium borate(LiBOB) was prepared by aqueous-phase method.The effect of material ratio,reaction temperature,reaction time and amount of crystallization solvent on the product quality under the condition of pilot test was studied.The result of products was confirmed by FTIR,TG-DSC and XRD.The pilot plant had achieved a production scale of 10 t/a at present.The experimental results showed the optimum operating parameters which were material ratio(the amount-of-substance ratio of oxalic acid to lithium carbonate to boric acid) of 4∶2∶1.1,reaction temperature of 80 ℃,reaction time of 8 h,the concentration amount(the mass ratio of residual solvent to total solvent mass) of about 80% in the process of concentration and crystallization,and the addition amount of crystallization agent of 4 times of the product mass.The dynamic drying was adopted for 8 h.After analysis,the quality of the product prepared by this process exceeded the level of the market products.
Yanrui Liu , Congcong Song , Guizhen Shi , Kun Wang . The study of double oxalate lithium borate preparation technology by aqueous phase method[J]. Inorganic Chemicals Industry, 2020 , 52(10) : 100 -105 . DOI: 10.11962/1006-4990.2019-0605
[1] | Fan Lizhen, Xing Taofeng, Rafi Awan. Studies on lithium bis(oxalato)-borate/propylene carbonate-based electrolytes for Li-ion batteries[J]. Ionics, 2011,17(6):491-494. |
[2] | 王艳菊, 乔庆东, 李琪, 等. 双乙二酸硼酸锂的合成及性能研究[J]. 化工新型材料, 2015,43(10):193-195. |
[3] | 平平. 锂离子电池热失控与火灾危险性分析及高安全性电池体系研究[D]. 合肥:中国科学技术大学, 2014. |
[4] | 邓凌峰, 陈洪, 魏银烨. 锂离子电池电解质锂盐双乙二酸硼酸锂的制备与性能[J]. 材料导报, 2009,23(S1):295-298. |
[5] | 宋洋, 赵连海, 梁子雷, 等. 双乙二酸硼酸锂在液态电解质中的研究进展[J]. 无机盐工业, 2009,41(10):11-14. |
[6] | 赵本好. 一种应用于电池电解液中环保型添加剂的性能研究[J]. 电池工业, 2017,21(3):9-11. |
[7] | 李世友, 马培华, 滕祥国, 等. 锂离子电池电解质的新型锂盐——双乙二酸硼酸锂[J]. 化学进展, 2007(5):695-699. |
[8] | Swiderska-Mocek A, Naparstek D. Physical and electrochemical properties of lithium bis(oxalate)borate-organic mixed electrolytes in Li-ion batteries[J]. Electrochimica Acta, 2016,204:69-77. |
[9] | Ulrich Wietelmann,Uwe Lischka,Marion Wegner, Lithium bisox alatoborate,the production thereof and its use as a conducting salt:US,6506516B1[P]. 2003-01-14. |
[10] | 张玥, 袁莉, 刘锦平, 等. 锂离子电池用双草酸硼酸锂的固相合成[J]. 无机盐工业, 2011,43(4):42-44. |
[11] | 陈姚, 杨倩韵, 于欣伟, 等. 两步法合成锂离子电池用双草酸硼酸锂[J]. 电池, 2016,46(5):251-254. |
/
〈 |
|
〉 |