Effect of PVDF structure on rheological properties of cathode slurry
Received date: 2020-03-19
Online published: 2020-09-27
The dispersible uniformity of cathode slurry of Li-ion battery has significant influence on the performance of bat-tery.Fine dispersible uniformity of cathode slurry of Li-ion battery relied on the adequate knowledge of rheological properties of slurry.Cathode slurry was prepared by using two commercial PVDF with different structure as binder,Li(Ni,Mn,Co)O2 as active material,carbon black as conducting additive(SP) and N-methy-2-pyrrolidone as solvent.The influence of PVDF structure on the rheological properties of cathode slurry of battery was analyzed using rotational rheometer.Results showed that,for steady shear,the slurry with branched PVDF as binder had higher zero-shear-rate viscosity and lower yield point than slurry with linear PVDF as binder,which meant slurry had higher anti-sedimentation and better fluidity.For oscillatory shear,slurry with linear PVDF as binder was prone to yield flow.SEM result showed that branched PVDF could bond with SP and active material to form a space conductive network,and the component distribution is more uniform.The research provided basis for technological optimization of storing and dispersion of Li-ion battery slurry.
Key words: cathode slurry; PVDF; Li-ion battery; rheological property
Jinwei Wang , Yuanyuan Xu , Gongwei Fu , Jian Zhou , Yong Yang . Effect of PVDF structure on rheological properties of cathode slurry[J]. Inorganic Chemicals Industry, 2020 , 52(9) : 57 -61 . DOI: 10.11962/1006-4990.2019-0515
[1] | Meng X, Yang X Q, Sun X. Emerging applications of atomic layer deposition for lithium-ion battery studies[J]. Advanced Materials, 2012,24(27):3589-3615. |
[2] | Kraytsberg A, Ein-Eli Y. Conveying advanced Li-ion battery mate-rials into practice the impact of electrode slurry preparation ski-lls[J]. Advanced Energy Materials, 2016,6(21):1600655. |
[3] | Liu Z, Battaglia V, Mukherjee P P. Mesoscale elucidation of the in-fluence of mixing sequence in electrode processing[J]. Langmuir, 2014,30(50):15102-15113. |
[4] | Gadkaree K P, Kadam R S, Poly-vinylidene difluoride anode binder in a lithium ion capacitor:US,9607778[P]. 2017-03-28. |
[5] | Yoo M, Frank C W, Mori S, et al. Effect of poly(vinylidene fluoride)binder crystallinity and graphite structure on the mechanical streng-th of the composite anode in a lithium ion battery[J]. Polymer, 2003,44(15):4197-4204. |
[6] | Yoo M, Frank C W, Mori S, et al. Interaction of poly(vinylidene fluo-ride) with graphite particles.2.effect of solvent evaporation kinetics and chemical properties of PVDF on the surface morphology of a composite film and its relation to electrochemical performance[J]. Chemistry of Materials, 2004,16(10):1945-1953. |
[7] | Bauer W, Notzel D. Rheological properties and stability of NMP ba-sed cathode slurries for lithium ion batteries[J]. Ceramics Interna-tional, 2014,40(3):4591-4598. |
[8] | 梁大宇. PVDF黏结剂含量对锂离子电池正极浆料流变性能的影响研究[J]. 无机盐工业, 2016,48(8):77-78. |
[9] | 娄立娟, 刘建叶, 俞炜, 等. 聚合物长支链的流变学表征方法[J]. 高分子通报, 2009(10):15-23. |
[10] | Cho K Y, Kwon Y I, Youn J R, et al. Interaction analysis between binder and particles in multiphase slurries[J]. The Analyst, 2013,138(7):2044-2050. |
[11] | Kwon Y I, Kim J D, Song Y S. Agitation effect on the rheological be-havior of lithium-ion battery slurries[J]. Journal of Electronic Ma-terials, 2015,44(1):475-481. |
[12] | 金日光, 华幼卿. 高分子物理[M].2版. 北京: 化学工业出版社, 2000. |
[13] | 杨乐, 魏江涛, 罗筑, 等. 高密度聚乙烯的熔融支化及其对性能的影响[J]. 高分子学报, 2017(8):1339-1349. |
[14] | 张沿江, 武行兵, 张金龙, 等. 锂离子电池浆料稳定性能研究[J]. 无机盐工业, 2015,47(5):72-74. |
[15] | 黄金元. 聚丙二醇共混聚丙烯腈原丝和预氧丝的制备及其结构与性能研究[D]. 上海:东华大学, 2011. |
[16] | Zheng H, Yang R, Liu G, et al. Cooperation between active materi-al,polymeric binder and conductive carbon additive in lithium ion battery cathode[J]. Journal of Physical Chemistry C, 2012,116(7):4875-4882. |
/
〈 |
|
〉 |