Catalytic Materials

Synthesis of NaY zeolite from preformed kaolin by dry gel conversion

  • Yaori Zhang ,
  • Jiazhong Zang ,
  • Lijuan Zhang ,
  • Meihua Hong ,
  • Haibin Yu
Expand
  • 1. CenerTech Tianjin Chemical Research and Design Institute Co.,Ltd.,Tianjin 300131,China
    2. Tianjin Refining and Catalytic Technology Engineering Center

Received date: 2020-02-22

  Online published: 2020-08-12

Abstract

Monolithic NaY zeolite was synthesized by dry gel conversion method.XRD,SEM and XRD were used to study the raw materials and products.The influences of n(SiO2)/n(Al2O3),n(Na2O)/n(SiO2),water content,crystallization temperature and crystallization time on the preparation of monolithic NaY zeolite were systematically investigated.Experimental results showed that when n(SiO2)/n(Al2O3) of synthesis system was 7.5,the n(SiO2)/n(Al2O3) of framework was 6.12.The crystallinity of the NaY zeolite increased with the amount of n(Na2O)/n(SiO2) firstly.If n(Na2O)/n(SiO2) was above 0.35,the NaY zeolite would turn to P zeolite.When the crystallization temperature increased from 90 ℃ to 120 ℃,the crystallinity of product increased accordingly.After crystallization at 110 ℃ for 20 h,the crystallinity of product was 98% and stated stable.Water was the key factor in the process of dry gel conversion.When the n(H2O)/n(SiO2) reached about 4.2,it was good for the synthesis of NaY zeolite.

Cite this article

Yaori Zhang , Jiazhong Zang , Lijuan Zhang , Meihua Hong , Haibin Yu . Synthesis of NaY zeolite from preformed kaolin by dry gel conversion[J]. Inorganic Chemicals Industry, 2020 , 52(8) : 88 -92 . DOI: 10.11962/1006-4990.2019-0495

References

[1] Xu Ruren, Pang Wenqin, Yu Jihong, et al. Chemistry of zeolites and related porous materials:synbook and structure[M]. Singapore:Wiley, 2007.
[2] Jin Junsu, Peng Chaoyun, Wang Jiujiang, et al. Facile synjournal of mesoporous zeolite Y with improved catalytic performace for heavy oil fluid catalytic cracking[J]. Industrial & Engineering Chemistry Research, 2014,53(8):3405-3411.
[3] Xu Wenyang, Dong Jinxiang, Li Jinping, et al. A novel method for the preparation of zeolite ZSM-5[J].Journal of the Chemical Society Chemical Communications, 1990(10):755-756.
[4] Zhou Jian, Hua Zile, Shi Jianlin, et al. Synjournal of a hierarchical micro/mesoporous structure by steam-assisted post-crystallization[J]. Chemistry, 2009,15(47):12949.
[5] Koekkoek A J J, Degirmenci V, Hensen E J M. Dry gel conversion of organosilane templated mesoporous silica:From amorphous to crystalline catalysts for benzene oxidation[J]. Journal of Materials Chemistry, 2011,21(25):9279-9289.
[6] M?ller K, Yilmaz B, Jacubinas R M, et al. One-step synjournal of hierarchical zeolite beta via network formation of uniform nanocrystals[J]. Journal of the American Chemical Society, 2011,133(14):5284-5295.
[7] Majano G, Mintova S, Bein T, Klap?tke T. High-density energeticmaterial hosted in pure silica mfi-type zeolite nanocrystals[J]. Advanced Materials, 2006,18(18):2440-2443.
[8] Chou C, Cundy C S, Garforth A A. A dry gel synjournal route to mesoporous ZSM-5 catalysts[J]. Studies in Surface Science & Catalysis, 2005,156:393-400.
[9] Chou Y H, Cundy C S, Garforth A A, et al. Mesoporous ZSM-5 catalysts:Preparation,characterisation and catalytic properties.Part I:Comparison of different synjournal routes[J]. Microporous & Mesoporous Materials, 2006,89(1/2/3):78-87.
[10] 戴长禄, 钟洪祥, 潘杰文, 等. 高岭土[M]. 北京: 中国建筑出版社, 1983.
[11] 郑淑琴. 高岭土碱溶性能对原位晶化的影响[J]. 石油化工, 2003,32(增刊):942-943.
[12] 郑淑琴. FCC催化剂中高岭土的影响及应用[J]. 非金属矿, 2002,25(2):22-23.
[13] Valtchev V P, Bozhilov K N. transmission electron microscopy study of the formation of fau-type zeolite at room temperature[J]. Journal of Physical Chemistry B, 2004,108(40):15587-15598.
[14] Hu Dan, Xia Qinghua, Lu Xinhua, et al. Synjournal of ultrafine zeolites by dry-gel conversion without any organic additive[J]. Materials Research Bulletin, 2008,43(12):3553-3561.
Outlines

/