Inorganic Chemicals Industry >
Inorganic oxidizer and reducing agent used in preparation of graphene
Received date: 2020-02-10
Online published: 2020-08-12
The chemical oxidation and reduction method that is having the advantages of wider source of raw materials,lower cost,higher yield and easier scaling up will be a future direction of preparing grapheme.The inorganic oxidizer and reducing agent used in preparation of grapheme as well as their principals and chemical reactions were summarized.The direction of improvement of the inorganic oxidizer and reducing agent used in preparation of grapheme was proposed for practical application purposes. A new type of oxidizer K2FeO4 and a new type of reducing agent Si were introduced to push on green manufacturing of grapheme and its complex materials.It was suggested paying attention promotion of grapheme industry to inorgan ic chemical industry.It was suggested strengthening applied basic research of grapheme modified oxide complex materials.
Key words： graphene; oxidizer; reducing agent
Jiansheng Li , Shaomei Yu , Xin Wang , Xiaodong Zu , Bingguang Liu . Inorganic oxidizer and reducing agent used in preparation of graphene[J]. Inorganic Chemicals Industry, 2020 , 52(8) : 6 -10 . DOI: 10.11962/1006-4990.2019-0508
| [1] | 杜淼, 张光荣. 石墨烯的制备及其应用研究进展[J]. 无机盐工业, 2019,51(3):12-15. |
| [2] | Tabinda Sattar. Current review on synjournal,composites and multi functional properties of graphene[J]. Topics in Current Chemistry, 2019,337(2):1-45. |
| [3] | 钟雨嘉, 朱宏伟. 石墨烯的结构、性能及潜在应用[J]. 物理, 2018,47(11):704-714. |
| [4] | Madhuri Sharon, Maheshwar Sharon. 石墨烯:改变世界的材料[M]. 张纯辉,沈启慧译.北京:机械工业出版社, 2017. |
| [5] | Dimiev A M, Eigler S. 氧化石墨烯基本原理与应用[M]. 张强强,何平鸽,杨凯淳译.北京:机械工业出版社, 2018. |
| [6] | 孙红娟, 彭同江. 石墨氧化-还原法制备石墨烯材料:制备过程中产物分析、结构和性质的演变及应用[M]. 北京: 科学出版社, 2015. |
| [7] | Gaston G L, Sacchi B, Peuvot K, et al. Experimental review:Chemical reduction of graphene oxide(GO) to reduced graphene oxide (rGO) by aqueous chemistry[J]. Nanoscale, 2017,9(27):9562-9571. |
| [8] | Kumar R, Joanni E, Singh R K, et al. Recent advances in the synjournal and modification of carbon-based 2D materials for application in energy conversion and storage[J]. Progress in Energy and Com bustion Science, 2018,67:115-157. |
| [9] | Abraham Jalbout. Method for cost-efficient industrial production of gr aphite oxide,grapheme oxide and graphing：US,201800230014A1[P]. 2018-08-16. |
| [10] | Tour J M, Kosynkin D V. Highly oxidized grapheme oxide and me thods for production thereof：US,9428394B2[P]. 2016-08-30. |
| [11] | 钟玲珑.改进的氧化石墨烯的制备方法:中国,106915741A[P]. 2017-07-04. |
| [12] | 于韶梅, 邢译, 李建生, 等.一种磁性石墨烯的制备方法:中国,110127678A[P]. 2019-08-16. |
| [13] | 于韶梅, 王欣, 李建生, 等.一种活性石墨烯的清洁生产方法:中国,109292766A[P]. 2019-02-01. |
| [14] | Tour J M, Dimiev A, Ceriotti G, et al.Production of grapheme nanoplatelets by oxidative anhydrous acidic media:US,201500360956A1[P]. 2015-12-17. |
| [15] | Gunda R, Madireddy B S, Dash R K . Synjournal of graphene oxide and reduced graphene oxide using volumetric method by a novel approach without NaNO2 or NaNO3[J]. Applied Nanoscience, 2018,8(4):751-758. |
| [16] | Peng L, Xu Z, Liu Z, et al. An iron-based green approach to 1-h production of single-layer graphene oxide[J]. Nature Communica tions, 2015,6:5716. |
| [17] | Yu C, Wang C F, Chen S. Facile access to graphene oxide from ferro-induced oxidation[J]. Scientific Reports, 2016,6:17071. |
| [18] | Sofer Z, Luxa J, Jankovsky O, et al. Synjournal of graphene oxide by oxidation of graphite with ferrate(Ⅵ) compounds:Myth or reali ty?[J]. Angewandte Chemie International Edition, 2016,55(39):11965-11969. |
| [19] | Hu C Y, Zhou R, Fan C J, et al. Influence of reducing reagent combination in graphene oxide reduction[J]. Micro & Nano Letters, 2016,11(4):215-220. |
| [20] | Korucu H, Simsek B, Kocakerim M M, et al. Effective reduction of graphene oxide using sulfur dioxide-containing chemical compounds[J].International journal of Environmental Science and Tech nology, 2019(11):1-14. |
| [21] | Dong L L, Chen W G, Deng N, et al. A novel fabrication of grap hene by chemical reaction with a green reductant[J]. Chemical Engineering Journal, 2016,306:754-762. |
| [22] | Pan Hui, Liu Ruiqi, Li Guanglong, et al. Simultaneous surface modification and chemical reduction of graphene oxide using gluco se[J]. Journal of Nanoscience and Nanotechnology, 2018,18(5):3356-3361. |
| [23] | Sriwong C, Choojun K, Kongtaweelert S . Investigation of the influences of reaction temperature and time on the chemical reduction of graphene oxide by conventional method using vitamin C as a re ducing agent[J]. Materials Science Forum, 2017,909:225-230. |
| [24] | 李永刚, 冯攀, 俞小花, 等. 不同还原剂还原的石墨烯电化学性能研究[J]. 化工新型材料, 2019,47(1):92-95. |
| [25] | 屈杨, 汪伟伟, 杨茂萍. 不同还原方法制备石墨烯及其电化学性能[J]. 电源技术, 2018,42(7):932-936. |
| [26] | 王欣, 李仕增, 李建生, 等.一种石墨烯掺杂玻璃镀膜液及其制备方法:中国,109206017A[P]. 2019-01-15. |
| [27] | 李霞, 祖晓冬, 李建生, 等.一种石墨烯掺杂纳米氧化物镀膜液及薄膜的制备方法:中国,109486248A[P]. 2019-03-19. |
| [28] | 于韶梅, 李建生, 邢译, 等.一种同时制备石墨烯和二氧化氯的方法:中国, 109956468A[P]. 2019-07-02. |
| [29] | 李建生, 刘炳光, 王少杰, 等. 大面积FTO透明导电薄膜制备技术研究进展[J]. 无机盐工业, 2017,49(8):1-4. |
| [30] | 李建生, 张发荣, 刘建东, 等.一种石墨烯和氟共掺杂氧化锡透明导电薄膜的制备方法:中国, 109524170A[P]. 2019-03-26. |
/
| 〈 |
|
〉 |