Effect of thermal activated temperature on activation and mechanism of red mud from alumina production
Received date: 2019-03-26
Online published: 2020-06-10
The effect and activation mechanism of thermal activated temperature on activity of red mud were analyzed.Phase transition temperature of red mud was analyzed by TG-DTA,and the changes of mineral composition and bond energy were also analyzed by XRD and FT-IR.Activity index was to assess the reactive activity of red mud.The test results showed that the diffraction peaks of dicalcium silicate was intensified after thermal activation.Calcite was decomposed into unstable and highly active substances. The stability of Si—O and Al—O bond were reduced.The activity index of activated red mud increased with the rising of activation temperature when it was no more than 700 ℃.Comparing with original red mud,the activity index of red mud activated at 700 ℃ increased 19.1%.While,the activity index of activated red mud decreased sharply when the thermal activation temperature was over 800 ℃.
Key words： red mud; thermal activation; activity index
Ran Hai , Shuaiqi Wang , Pan Liu , Junxia Liu . Effect of thermal activated temperature on activation and mechanism of red mud from alumina production[J]. Inorganic Chemicals Industry, 2019 , 51(9) : 72 -75 . DOI: 10.11962/1006-4990.2018-0584
| [1] | 钟晨, 夏举佩 . 拜耳法赤泥中Na+的浸出实验研究[J]. 硅酸盐通报, 2013,32(10):2012-2015. |
| [2] | 海然, 刘俊霞, 李建伟 . 氧化铝赤泥放射性及其屏蔽机制研究现状[J]. 无机盐工业, 2016,48(9):10-12. |
| [3] | 吴素彬, 聂登攀, 王振杰 , 等. 逆流浸取法回收赤泥中的碱[J]. 化工进展, 2014,33(6):1607-1609. |
| [4] | 闫军 . 碱激发赤泥胶凝材料的探索研究[J].轻金属, 2011(增刊):147-151. |
| [5] | 刘晓明, 孙恒虎, 冯向鹏 , 等. 赤泥最佳热处理工艺制度研究[J]. 稀有金属材料与工程, 2007,36(增刊1):983-986. |
| [6] | 杨芳, 韩涛, 靳秀芝 , 等. 热活化对赤泥物相及活性的影响[J].粉煤灰综合利用, 2015(2):3-6. |
| [7] | 申建立 . 赤泥基胶凝材料制备技术研究[D]. 北京:中国矿业大学, 2012. |
| [8] | Ribeiro D V, Silva A S, Labrincha J A , et al. Rheological properties and hydration behavior of portland cement mortars containing calcined redmud[J]. Canadian Journal of Civil Engineering, 2013,40(6):557-566. |
| [9] | 李绍纯, 张国立, 赵铁军 , 等. 拜耳法赤泥活化方式对水泥基材料性能的影响[J].混凝土, 2013(6):29-32. |
| [10] | 刘俊霞, 刘明清, 杨延娟 , 等. 硫酸氢钠对黄河泥沙工程特性的改性及机理研究[J]. 建筑材料学报, 2017,20(2):204-209. |
| [11] | 展光美 . 赤泥地聚合物制备技术及耐久性试验研究[D]. 北京:中国矿业大学, 2016. |
| [12] | Davidovits J . Geopolymer chemistry and applications[M]. Saint-Quentin:Geopolymer Institute, 2011. |
| [13] | Panias D.Giannopoulou I P, Perraki T . Effect of synjournal parameters on the mechanical properties of fly ashbased geopolymers[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspe cts, 2007,301(1/2/3):246-254. |
| [14] | Vu D D, Stroven P, Bui V B . Strength and durability aspects of ca lcined kaolin blended Portland cement mortar and concrete[J]. Cement & Concrete Composites, 2001,4(23):471-478. |
/
| 〈 |
|
〉 |