Inorganic Chemicals Industry >
Study on strengthening technology of raw coal gangue aggregate
Received date: 2019-10-28
Online published: 2020-04-22
The original coal gangue in Tongchuan,Shaanxi Province was taken as the research object.Through the processing of sorting,crushing and grading etc.,the experiments on chemical strengthening and surface coating of coal gangue were em-phasized.In this study,coal gangue with the particle size of 2.36~4.75 mm was selected.The strength and water resistance of coal gangue were improved with different strengthening agents and coated powder.It was found that when the solution was compounded with 0.7% soil solidified agent in a mass fraction of 6% silicate-based strengthening agent B,the strengthening effect on coal gangue was the most obvious.The surface of the coal gangue after liquid strengthening was covered with a mass ratio of cement to tailings powder of 1:1.2,The amount of coating was 25% of the mass of coal gangue.The dry crush value of the obtained product can be reduced by about 50%,the water resistance performance was improved by about 85%,and the produced coal gangue aggregate product performance was well.The coal gangue aggregate product was replaced by a part of the stone as a cement mortar aggregate.Compared with the original gangue cement mortar,the reinforced coal gangue cement mortar has improved flexural strength and compressive strength.
Key words： coal gangue; crushing value; water resistance; liquid strengthener; cover treatment
Xiaoting Liu , Jiuran Wen , Siyu Wang , Kaiping Liu , Ni Gao , Jiaqiang Zhong . Study on strengthening technology of raw coal gangue aggregate[J]. Inorganic Chemicals Industry, 2020 , 52(4) : 65 -71 . DOI: 10.11962/1006-4990.2019-0489
| [1] | 孙志华, 刘开平, 汪敏强 , 等. 铜川自燃煤矸石特征研究[J]. 煤炭学报, 2013,38(S1):136-141. |
| [2] | 邱景平, 李小庆, 孙晓刚 , 等. 煤矸石资源化利用现状与进展[J]. 有色金属:矿山部分, 2014,66(1):47-50. |
| [3] | 罗顺, 游玉萍, 林义民 , 等. 我国工业固废的产业规模和处理技术现状[J]. 材料研究与应用, 2018,12(3):178-182. |
| [4] | 段晓牧 . 煤矸石集料混凝土的微观结构与物理力学性能研究[D]. 徐州:中国矿业大学, 2014. |
| [5] | 陈彦文, 牛晚扬, 丁兆阳 . 煤矸石混凝土弹性模量的试验研究[J].混凝土, 2016(4):20-23. |
| [6] | 刘世, 刘海卿, 邢粟 . 煤矸石混凝土水分传输及分布预测[J]. 硅酸盐通报, 2018,37(3):786-791. |
| [7] | 董作超 . 煤矸石集料混凝土的力学性能与抗碳化试验研究[D]. 徐州:中国矿业大学, 2016. |
| [8] | 王生新, 吕擎峰, 王得楷 , 等. 水玻璃固化黏土矿物的试验研究[J]. 中南大学学报:自然科学版, 2013,44(7):2656-2662. |
| [9] | 卜思敏 . 纳米硅溶胶固化黄土的强度特性及其固化机理[D]. 兰州:兰州大学, 2016. |
| [10] | 吴朱敏 . 改性水玻璃固化黄土研究[D]. 兰州:兰州大学, 2013. |
| [11] | 吴朱敏, 吕擎峰, 王生新 . 复合改性水玻璃加固黄土微观特征研究[J]. 岩土力学, 2016,37(S2):301-308. |
| [12] | 刘志琦, 董宝中 . 离子类土壤固化剂的固化机理及发展[J]. 四川建材, 2018,44(11): 101, 103. |
| [13] | 李霖皓, 龙广成, 白朝能 , 等. 干湿循环作用下煤矸石及其与水泥石之间界面的耐久性研究[J]. 煤炭工程, 2019,51(6):153-159. |
| [14] | 崔孝炜, 狄燕清, 庞华 , 等. 用某钼尾矿制备高性能混凝土的试验[J]. 金属矿山, 2017(7):193-196. |
/
| 〈 |
|
〉 |