Preparation of T-type zeolite membrane and its separation performance on acetonitrile-water containing acid

  • Yihua Zang ,
  • Zan Chen ,
  • Chunguang Sheng ,
  • Wei Wu ,
  • Qiuhong Zheng ,
  • Liangming Wang
Expand
  • 1. CenerTech Tianjin Chemical Research and Design Institute Co.,Ltd.,Tianjin 300131,China
    2. Heilongjiang Nhu Biotechnology Company Ltd.

Received date: 2019-08-26

  Online published: 2020-02-26

Abstract

A large amount of acetonitrile waste liquid will be produced in petrochemical and pharmaceutical industries,which can be recovered by inorganic molecular sieve membrane separation technology to create considerable economic value.Howe-ver,acetonitrile waste liquid has high water content and acidity.NaA zeolite membrane can not be used in this system for a long time,which is widely used at present.The self-made T-type zeolite with an average particle size of 600 nm was used as crystal seed.The crystal seed was loaded on the surface of α-Al2O3 carrier tube by vacuum coating method.The T-type zeolite membrane was prepared by hydrothermal crystallization at 150 ℃ for 16 h.And pervaporation evaluation experiments were carried out.The results showed that the pervaporation dehydration of acetonitrile mixed solution containing 1%(mass fraction)acetic acid and 10%(mass fraction) water was carried out by self-made T-type zeolite membrane at 100 ℃.The permeation flux was 2.51 kg/(m 2·h).During 120 h operation,the separation factor maintained above 2 250,and the performance of T-type zeolite membrane remained basically unchanged.

Cite this article

Yihua Zang , Zan Chen , Chunguang Sheng , Wei Wu , Qiuhong Zheng , Liangming Wang . Preparation of T-type zeolite membrane and its separation performance on acetonitrile-water containing acid[J]. Inorganic Chemicals Industry, 2020 , 52(2) : 50 -53 . DOI: 10.11962/1006-4990.2019-0103

References

[1] 李华青, 孙纯红, 吴绍帅 . 工业废弃乙腈回收提纯工艺技术研究进展[J]. 山东化工, 2017,46(1):62-64.
[2] Wenten I G, Dharmawijaya P T, Aryanti P T P , et al. LTA zeolite membranes:current progress and challenges in pervaporation[J]. RSC Advances, 2017,47(7):29520-29539.
[3] Kondo M, Kita H . Permeation mechanism through zeolite NaA and T-type membranes for practical dehydration of organic solvents[J]. Journal of Membrane Science, 2010,361(1/2):223-231.
[4] Mirfendereski S M, Mazaheri T, Sadrzadeh M , et al. CO2 and CH4 permeation through T-type zeolite membranes:Effect of synjournal parameters and feed pressure[J]. Separation and Purification Technology, 2008,61(3):317-323.
[5] Wang X R, Chen Y Y, Zhang C , et al. Preparation and characteriza-tion of high-flux T-type zeolite membranes supported on YSZ hollow fibers[J]. Journal of Membrane Science, 2014,455:294-304.
[6] Cui Y, Kita H, Okamoto K . Zeolite T membrane:Preparation,char acterization,pervaporation of water/organic liquid mixtures and acid stability[J]. Journal of Membrane Science, 2004,236(1/2):17-27.
[7] 周荣飞, 胡娜, 袁慧 , 等. T 型分子筛膜的合成,表征与渗透汽化性能[J]. 无机化学学报, 2009,25(8):1439-1446.
[8] 张飞, 郑艺鸿, 桂田 , 等. 含氟体系中高性能 T 型分子筛膜的合成[J]. 无机化学学报, 2014,30(8):1845-1854.
[9] 郭大鹏, 周志辉, 吴建雄 , 等. 热浸渍预涂晶种温度对 T 型分子筛膜性能的影响[J]. 石油化工, 2014,43(8):903-907.
[10] 吕尤佳, 李华征, 杨建华 , 等. 清液体系高性能 T 型分子筛膜的制备及表征[J]. 无机材料学报, 2016,31(7):705-710.
Outlines

/