静爆剂中氧化钙在不同煅烧条件下的性能研究

doi:10.19964/j.issn.1006-4990.2022-0691

Abstract

Abstract:

Calcite was calcined by using KRX-17B high temperature electric furnace vacuum environment under different calcination conditions to fire calcium oxide clinker，the hydration activity test showed that when the calcination temperature was decreased from 1 300 ℃ to 1 200 ℃，the calcium oxide hydration reaction rate was changed like“jumping”，the evolution of calcium oxide clinker micromorphology under different calcination conditions were observed and analyzed by tungsten filament scanning electron microscope（SEM），and it was found that the higher the calcination temperature and the longer the constant temperature time，the calcium oxide clinker matrix changed from loose，porous and agglomeration to strict and dense.“Thermal effect”could explain the effect of temperature on calcium oxide′s hydration resistance and swelling properties.The expansion pressure of the prepared roll static crusher measured by“outer pipe method” showed that the constant temperature time was constant，when the clinker calcination temperature was increased from 1 300 ℃ to 1 500 ℃，the expansion pressure of the prepared roll crusher was increased by 25.6 MPa.The calcination temperature was certain，when the constant temperature time was extended from 5 h to 25 h，the expansion pressure of the prepared roll static crusher was increased by 23.4 MPa.

Key words: calcium oxide, high temperature calcination conditions, hydration resistance, rolling up with static crushing agent, expansion pressure

CLC Number:

TQ132.32

DU Guanggang, HE Tong, XU Zehui, LIU Lei. Study on properties of calcium oxide in SCA under different calcination conditions[J]. Inorganic Chemicals Industry, 2023, 55(10): 35-41.

Figures/Tables 9

Fig.1

Fig.2

Fig.3

Fig.4

Table 1

Fig.5

Table 2

Fig.6

Fig.7

References 34

1	曲晓龙，于海斌，臧甲忠，等.改性氧化钙脱硫剂制备及性能研究［J］.无机盐工业，2018，50（11）：31-33.
	QU Xiaolong， YU Haibin， ZANG Jiazhong，et al.Preparation and performance of modified calcium oxide desulfurizer［J］.Inorganic Chemicals Industry，2018，50（11）：31-33.
2	莫雅超，闫君，赵长颖.CaO/Ca（OH）₂核壳结构颗粒的制备及其储热性能［J］.储能科学与技术，2022，11（12）：3828-3835.
	MO Yachao， YAN Jun， ZHAO Changying.Preparation and thermal storage properties of CaO/Ca（OH）₂ core-shell-structured particl-es［J］.Energy Storage Science and Technology，2022，11（12）：3828-3835.
3	关江哲，朱桂花，吕硕，等.氧化钙对金属/粉煤灰基高温定形复合相变材料蓄热性能的影响［J］.硅酸盐通报，2020，39（9）：3008-3013，3022.
	GUAN Jiangzhe， ZHU Guihua， Shuo LÜ，et al.Effect of calcium oxide on thermal storage performance of metal/fly ash-based high temperature form-stable composite phase change material［J］.Bulletin of the Chinese Ceramic Society，2020，39（9）：3008-3013，3022.
4	李鹏程，叶义成，姚囝，等.膨胀型浆体膨胀性能及力学破坏特征试验研究［J］.矿冶工程，2020，40（6）：8-12.
	LI Pengcheng， YE Yicheng， YAO Nan，et al.Experimental research on expansion performance and mechanical failure characteristics of expansive slurry［J］.Mining and Metallurgical Engineering，2020，40（6）：8-12.
5	段宾，施翠莲，张双杰，等.兰炭粉与氧化钙制备电石的工艺研究［J］.无机盐工业，2019，51（1）：67-69，72.
	DUAN Bin， SHI Cuilian， ZHANG Shuangjie，et al.Study on preparation of calcium carbide from semi-coke and calcium oxide［J］.Inorganic Chemicals Industry，2019，51（1）：67-69，72.
6	徐国庆.静态破碎剂制备及力学性能研究［D］.哈尔滨：哈尔滨工程大学，2020.
	XU Guoqing.Preparation and mechanical properties of static crushing agent［D］.Harbin：Harbin Engineering University，2020.
7	田其哲，叶俊伟，宁桂玲.微波水热法制备氧化镁-氧化铜-氧化钙复合材料及其抗菌性能［J］.无机盐工业，2020，52（12）：12-16，39.
	TIAN Qizhe， YE Junwei， NING Guiling.Preparation and antibacterial properties of MgO-CuO-CaO composite by microwave hydrothermal method［J］.Inorganic Chemicals Industry，2020，52（12）：12-16，39.
8	NATANZI A S， LAEFER D F， CONNOLLY L.Cold and moderate ambient temperatures effects on expansive pressure development in soundless chemical demolition agents［J］.Construction and Buil- ding Materials，2016，110：117-127.
9	ARSHADNEJAD S， GOSHTASBI K， AGHAZADEH J.A model to determine hole spacing in the rock fracture process by non-explosive expansion material［J］.International Journal of Minerals，Metallurgy，and Materials，2011，18（5）：509-514.
10	GAMBATESE J A.Controlled concrete demolition using expansive cracking agents［J］.Journal of Construction Engineering and Management，2003，129（1）：98-104.
11	王玉杰.静态破裂技术及机理研究［D］.武汉：武汉理工大学，2009.
	WANG Yujie.Reseach on mechanism and technology of non-explosive demolition［D］.Wuhan：Wuhan University of Technology，2009.
12	SCHIELE E， BERENS L W.石灰［M］.陆华，武洞明译.北京：中国建筑工业出版社，1981.
13	李华，田倩，张守治.氧化钙膨胀熟料水化动力学及微观分析［J］.混凝土，2014（3）：75-78，83.
	LI Hua， TIAN Qian， ZHANG Shouzhi.Hydration kinetics and microscopic analysis of calcium oxide expansion clinker［J］.Concrete，2014（3）：75-78，83.
14	施惠生.氧化钙的显微结构与水化活性［J］.硅酸盐学报，1994，22（2）：117-123.
	SHI Huisheng.Microstructure and hydration activity of CaO［J］.Journal of the Chinese Ceramic Society，1994，22（2）：117-123.
15	张悦，李恩军，李先容，等.烧结温度对纯氧化钙性能的影响［J］.中国陶瓷工业，2015，22（3）：13-16.
	ZHANG Yue， LI Enjun， LI Xianrong，et al.Effect of sintering temperature on the properties of pure CaO［J］.China Ceramic Industry，2015，22（3）：13-16.
16	孙立新.静态破碎剂的研制及应用［D］.西安：西安建筑科技大学，2005.
	SUN Lixin.Study on the static cracking agent and its application［D］.Xi'an：Xi'an University of Architecture and Technology，2005.
17	王作鹏，杜华善，张现亭，等.一种新型静态破碎剂的研制［J］.煤矿爆破，2004（2）：13-15.
	WANG Zuopeng， DU Huashan， ZHANG Xianting，et al.Developing of a new static cracking agent［J］.Coal Mine Blasting，2004（2）：13-15.
18	李胜，李宗杰，罗明坤.煤岩静态破碎剂合理组分及配比实验研究［J］.爆破，2018，35（1）：137-141，153.
	LI Sheng， LI Zongjie， LUO Mingkun.Experimental study on reasonable composition and proportion of coal and rock static cracking agent［J］.Blasting，2018，35（1）：137-141，153.
19	张锦瑞.介绍几种静态破碎剂［J］.化工矿山技术，1994，23（1）：63.
20	罗明坤，李胜，李宗杰，等.煤岩致裂中的静态破碎剂组分及其性能［J］.工程爆破，2017，23（3）：5-9.
	LUO Mingkun， LI Sheng， LI Zongjie，et al.Composition and performance of static cracking agent in coal and rock fracturing［J］.Engineering Blasting，2017，23（3）：5-9.
21	马丽洁，左安家，李昊，等.静态膨胀剂的影响因素试验研究与分析［J］.石油化工应用，2022，41（1）：104-109.
	MA Lijie， ZUO Anjia， LI Hao，et al.Experimental study on crack initiation effect of static expansion agent in borehole［J］.Petrochemical Industry Application，2022，41（1）：104-109.
22	李阳阳.水温与水剂比对静态破碎剂膨胀性能影响的试验研究［J］.建井技术，2019，40（1）：32-35，22.
	LI Yangyang.Experimental study on influence of water temperature and water agent ratio on expansion performance of soundless cracking agent［J］.Mine Construction Technology，2019，40（1）：32-35，22.
23	葛进进，徐颖，郑志涛.水剂比对静态破碎效果影响的试验研究［J］.煤炭技术，2017，36（2）：175-176.
	GE Jinjin， XU Ying， ZHENG Zhitao.Experimental research on influences of water agent ratio on static cracking effect［J］.Coal Technology，2017，36（2）：175-176.
24	郑志涛，徐颖，倪红娟.钻孔直径对静态破碎剂致裂性能影响试验分析［J］.科学技术与工程，2016，16（2）：7-10，23.
	ZHENG Zhitao， XU Ying， NI Hongjuan.Test and analysis of hole diameter effect on cracking performance of static cracking age-nt［J］.Science Technology and Engineering，2016，16（2）：7-10， 23.
25	施惠生，赵玉静，沙丹丹.游离氧化钙对水泥浆体体积膨胀的影响机制［J］.水泥，2000（4）：1-3.
	SHI Huisheng， ZHAO Yujing， SHA Dandan.Effect of free CaO on the volumetric expansion of cement pastes［J］.Cement，2000（4）：1-3.
26	马志钢，王瑾.试论静态破碎剂及其性能改进［J］.煤矿爆破，2002（1）：4-6.
27	DENG Min， HONG Dongwen， LAN Xianghui，et al.Mechanism of expansion in hardened cement pastes with hard-burnt free lime［J］.Cement and Concrete Research，1995，25（2）：440-448.
28	CHATTERJI S.Mechanism of expansion of concrete due to the presence of dead-burnt CaO and MgO［J］.Cement and Concrete Research，1995，25（1）：51-56.
29	郑文忠，李瑞森，徐笠博，等.静态破碎技术研究综述与建议［J］.哈尔滨工业大学学报，2021，53（5）：190-200.
	ZHENG Wenzhong， LI Ruisen， XU Libo，et al.Review and analysis on research and application of static crushing technology［J］.Journal of Harbin Institute of Technology，2021，53（5）：190- 200.
30	徐香新.静态破碎剂膨胀力学行为的研究及应用［D］.沈阳：东北大学，2014.
	XU Xiangxin.Research and application on expansion mechanical behaviors of static cracking agent［D］.Shenyang：Northeastern University，2014.
31	徐芝纶.弹性力学：上册［M］.4版.北京：高等教育出版社，2006.
32	游宝坤.静态爆破技术：无声破碎剂及其应用［M］.北京：中国建材工业出版社，2008.
33	杨泽波，辜振睿，王海龙.离子掺杂对钙质膨胀剂熟料性能的影响［J］.材料导报，2021，35（S2）：259-261.
	YANG Zebo， GU Zhenrui， WANG Hailong.Effect of ion doping on the properties of calcium expanding agent clinker［J］.Materials Reports，2021，35（S2）：259-261.
34	刘加平，郭舒，田倩，等.氧化钙膨胀熟料的水化动力学［J］.建筑材料学报，2014，17（1）：15-18.
	LIU Jiaping， GUO Shu， TIAN Qian，et al.Hydration kinetics of CaO expansion clinker［J］.Journal of Building Materials，2014，17（1）：15-18.

煅烧温度/℃	密度/（g∙cm^-3）
1 300	1.26
1 400	1.36
1 500	1.58

恒温时间/ h	方解石表观密度/ （g∙cm^-3）（理论值）	熟料密度/ （g∙cm^-3）
5	2.61	1.58
10	2.61	1.67
15	2.61	1.75
20	2.61	1.82
25	2.61	1.91

[1]	LI Qiang, YOU Xiaomin, SHE Xuefeng, JIANG Zeyi, XUE Qingguo, WANG Jingsong. Effect of calcination temperature and carbon structure on compressive strength of CaO-containing carbon pellets [J]. Inorganic Chemicals Industry, 2023, 55(9): 43-49.
[2]	CHEN Qi, LIAO Dankui, ZHANG Qingnian, YAN Jinsheng, HUANG Yu, CHEN Xiaopeng, TONG Zhangfa. Fast and efficient determination of quicklime activity by conductivity method [J]. Inorganic Chemicals Industry, 2023, 55(9): 114-120.
[3]	CHEN Xiaoqing, ZHOU Jian′an, WANG Yi, HAN Juan, WANG Bao, PEI Peiyan. Study on decomposition characteristic of limestone powder in high temperature flue gas of converter [J]. Inorganic Chemicals Industry, 2023, 55(10): 70-77.
[4]	ZENG Yanjie,XU Tongfei,HUANG Ziliang,CHEN Zhipeng,LIU Xudong,YI Meigui. Study on removal of calcium impurities from magnesium waste residue by roasting-hydration complexing [J]. Inorganic Chemicals Industry, 2022, 54(11): 118-123.
[5]	Meng Hua,Zhao Jingyi,Nie Chaoyang,Wang Ye. Study on simulation process of reducing titanium dioxide gypsum by sulfur fluidization [J]. Inorganic Chemicals Industry, 2021, 53(9): 61-66.
[6]	Zhang Yulu,Wang Ye,Yang Lin,Yang Xiushan,Wang Xinlong. Preparation of high purity calcium oxide combined with sulfuric acid from fluorine gypsum decomposed by sulfur [J]. Inorganic Chemicals Industry, 2020, 52(7): 70-73.
[7]	Su Shaolong,Qu Xiaolong,Zhong Dule,Sun Yanmin,Nan Jun,Li Shipeng. Study on preparation and performance of desulfurizers in process of calcium injection desulfurization in furnace [J]. Inorganic Chemicals Industry, 2020, 52(7): 66-69.
[8]	ZHENG Shao-Cong, NING Ping, WANG Fan, CHENG Fei-Xiang, HU Fen-E. Study on preparation of sulfur dioxide and lime by thermal decomposition of phosphogypsum [J]. INORGANICCHEMICALSINDUSTRY, 2013, 45(9): 45-.
[9]	TU Lan-Ying, ZHAO Qi-Wen, CUI Xiao-Qin. Experimental study on purifying by-product calcium chloride of soda ash [J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(8): 32-.
[10]	ZHAO Hui-Juan, LIU Can, WANG Kai, YANG Hong. Effect of CaF₂ on content of free CaO in tricalcium silicate by co-precipitation process [J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(8): 19-.
[11]	LU Yang, ZHANG Wei. Influence of activity of calcium oxide on solid state sintering reaction [J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(7): 16-.
[12]	DAI Hong-Xing, DENG Ji-Guang, ZHANG Lei, ZHAO Zhen-Xuan, WANG Guo-Zhi, LIU Cai-Xin, LI Hui-Ning. Soft/hard template assisted fabrication of porous MgO,CaO,and CaCO₃ [J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(5): 18-.
[13]	CAO Chun-Bao, ZHANG Wei, DENG Fu-Jun. Analysis on activity of calcium oxide from calcining small amount of limestone [J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(11): 19-.
[14]	Tian Weijun;Lai Naibin. Process research and production practice of recovering calcium oxide from carbide slag [J]. INORGANICCHEMICALSINDUSTRY, 2010, 0(8): 0-0.
[15]	Wang Hui. Comprehensive utilization of cryolite mother liquor [J]. INORGANICCHEMICALSINDUSTRY, 2009, 0(3): 0-0.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Study on properties of calcium oxide in SCA under different calcination conditions

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 9

References 34

Related Articles 15

Metrics

Comments

Recommended 0