NH3-SCR脱硝催化剂现状及中毒失活现象研究进展
收稿日期: 2021-12-06
网络出版日期: 2022-11-23
基金资助
国家自然科学基金(52076126);上海市科学技术委员会项目(20dz1205208)
Current situation of NH3-SCR denitration catalyst and research progress on poisoning and deactivation
Received date: 2021-12-06
Online published: 2022-11-23
随着国家能源深度调峰的推进并降低锅炉负荷运行，发现锅炉出口烟温难以驱动选择性催化还原脱硝反应的问题，通过综述氨选择性催化还原反应（NH3-SCR）催化剂在国内外的研究进展，发现单一贵金属催化剂温度窗口窄、易中毒和比表面积较小等问题影响了其催化活性，而复合的金属氧化物催化剂、新兴的生物炭催化剂和沸石催化剂具有多孔性和良好的稳定性等优点。催化剂脱硝机理可以简单表示为其表面的酸性位点吸附氨气和氧气并与之反应，催化剂的中毒原因可总结为其内部空隙被碱金属堵塞、金属氧化物被二氧化硫抢先反应和酸性位点被羟基覆盖，具体表现为催化剂的活性降低、吸附NH3的效率下降。对比了商用催化剂和新兴催化剂的脱硝性能得出结论，未来的研究方向是研发耐硫、耐水、耐碱的低温高效脱硝催化剂。
李可君 , 李芳芹 , 任建兴 , 刘鑫 , 陈林峰 , 蔡健明 . NH3-SCR脱硝催化剂现状及中毒失活现象研究进展[J]. 无机盐工业, 2022 , 54(11) : 18 -24 . DOI: 10.19964/j.issn.1006-4990.2021-0735
With the promotion of national energy deep peak shaving and the reduction of boiler load operation，it is found that the flue gas temperature at the outlet of the boiler is difficult to drive the selective catalytic reduction denitration reaction.By summarizing the research progress of NH3-SCR denitration catalyst at home and abroad，it was concluded that the single noble metal catalyst had the factors affecting its catalytic activity，such as narrow temperature window，easy poisoning characteristics and small specific surface area，while the composite metal oxide catalyst，the new biochar catalysts and zeolite catalysts had the advantages of porosity and good stability.The denitration mechanism of the catalyst could be simply expressed as that the acidic sites on its surface adsorbed gaseous NH3 and O2 and react with them.The poisoning causes of the catalyst could be summarized as that its internal voids were blocked by alkali metals，metal oxides were preempted by SO2 and the acidic sites were covered by hydroxyl groups.Specifically，the activity of the catalyst was decreased and the efficiency of NH3 adsorption was decreased.By comparing the denitration performance of commercial catalysts and emerging catalysts，it was concluded that the future research direction was to develop low-temperature and high-efficiency denitration catalysts with sulfur resistance，water resistance and alkali resistance.
Key words： SCR catalyst; denitration; low temperature; poisoning
| 1 | 葛挺.“十四五”期间火电技术发展方向分析[J].河南电力,2020(S2):1-3. |
| 1 | GE Ting.Analysis of the development direction of thermal power technology during the“14th Five-Year Plan” period[J].Henan Electric Power,2020(S2):1-3. |
| 2 | 姚小江,张雷,孔婷婷,等.低温氨-选择性催化还原氮氧化物催化剂的研究进展[J].工业催化,2016,24(6):1-9. |
| 2 | YAO Xiaojiang, ZHANG Lei, KONG Tingting, et al.Research progress in selective catalytic reduction of nitrogen oxides by ammonia at low temperature[J].Industrial Catalysis,2016,24(6):1-9. |
| 3 | 王金玉.掺杂Ce对Mn基脱硝催化剂抗水抗硫性的实验研究和模拟分析[D].青岛：青岛大学，2020. |
| 3 | WANG Jinyu.Experimental study and simulation analysis on water and sulfur resistance of Mn based denitration catalyst doped with Ce[D].Qingdao：Qingdao University，2020. |
| 4 | HAN Lupeng, CAI Sixiang, GAO Min, et al.Selective catalytic reduction of NO x with NH3 by using novel catalysts：State of the art and future prospects[J].Chemical Reviews,2019,119(19):10916-10976. |
| 5 | ODRIOZOLA J A, HEINEMANN H, SOMORJAI G A, et al.AES and TDS study of the adsorption of NH3 and NO on V2O5 and TiO2 surfaces：Mechanistic implications[J].Journal of Catalysis,1989,119(1):71-82. |
| 6 | PENG Yue, LI Junhua, SI Wenzhe, et al.Deactivation and regeneration of a commercial SCR catalyst：Comparison with alkali metals and arsenic[J].Applied Catalysis B：Environmental,2015,168/169: 195-202. |
| 7 | LARRUBIA M A, RAMIS G, BUSCA G.An FT-IR study of the adsorption of urea and ammonia over V2O5-MoO3-TiO2 SCR catalysts[J].Applied Catalysis B：Environmental,2000,27(3):L145-L151. |
| 8 | 梁冉冉.SCR催化剂脱硝及中毒机理的量子化学研究[D].北京：华北电力大学，2017. |
| 8 | LIANG Ranran.Quantum chemistry research on DeNO x and poisoning mechanism of SCR catalyst[D].Beijing：North China Electric Power University，2017. |
| 9 | OZKAN U S, CAI Yeping, KUMTHEKAR M W.Effect of crystal morphology in selective catalytic reduction of nitric oxide over V2O5 catalysts[J].Applied Catalysis A：General,1993,96(2):365-381. |
| 10 | 刘福东,单文坡,石晓燕,等.用于NH3选择性催化还原NO的非钒基催化剂研究进展[J].催化学报,2011,32(7):1113-1128. |
| 10 | LIU Fudong, SHAN Wenpo, SHI Xiaoyan, et al.Research progress in vanadium-free catalysts for the selective catalytic reduction of NO with NH3 [J].Chinese Journal of Catalysis,2011,32(7):1113-1128. |
| 11 | LIU Zhong, HAN Jian, ZHAO Li, et al.Effects of Se and SeO2 on the denitrification performance of V2O5-WO3/TiO2 SCR cataly-st[J].Applied Catalysis A：General,2019,587.Doi:10.1016/j.apcata.2019.117263. |
| 12 | XU Junqiang, CHEN Guorong, GUO Fang, et al.Development of wide-temperature vanadium-based catalysts for selective catalytic reducing of NO x with ammonia：Review[J].Chemical Engineering Journal,2018,353: 507-518. |
| 13 | LIU Guangli, HAN Dongtai, CHENG Jie, et al.Performance of C2H4 reductant in activated-carbon-supported MnO x -based SCR catalyst at low temperatures[J].Energies,2018,12(1).Doi:10.3390/en12010123. |
| 14 | 许硕.锰系催化剂的制备及其低温SCR脱硝性能的研究[D].哈尔滨：哈尔滨工程大学，2016. |
| 14 | XU Shuo.Research on Mn-based series catalysts and mechanism for selective catalytic reduction of NO x at low-temperature[D].Harbin：Harbin Engineering University，2016. |
| 15 | KAPTEIJN F, SINGOREDJO L, ANDREINI A, et al.Activity and selectivity of pure manganese oxides in the selective catalytic reduction of nitric oxide with ammonia[J].Applied Catalysis B：Environmental,1994,3(2/3):173-189. |
| 16 | THIRUPATHI B, SMIRNIOTIS P G.Nickel-doped Mn/TiO2 as an efficient catalyst for the low-temperature SCR of NO with NH3：Catalytic evaluation and characterizations[J].Journal of Catalysis,2012,288: 74-83. |
| 17 | LI Lulu, SUN Bowen, SUN Jingfang, et al.Novel MnO x -CeO2 nanosphere catalyst for low-temperature NH3-SCR[J].Catalysis Communications,2017,100: 98-102. |
| 18 | JIANG Haoxi, WANG Yaodong, ZHOU Jiali, et al.Morphology control of manganese-based catalysts for low-temperature selective catalytic reduction of NO x [J].Materials Letters,2018,233: 250-253. |
| 19 | 牟金成.新型铁基催化剂的制备及其低温NH3选择性催化还原NO x 研究[D].大连：大连理工大学，2020. |
| 19 | MOU Jincheng.Investigation on the preparation and application in low-temperature selective catalytic reduction of NO x with NH3 over novel Fe-based catalysts[D].Dalian：Dalian University of Technology，2020. |
| 20 | SHAVEL A, LIZ-MARZáN L M.Shape control of iron oxide nanoparticles[J].Physical Chemistry Chemical Physics：PCCP,2009,11(19):3762-3766. |
| 21 | YANG Xingye, LI Bin, SUN Liang, et al.Effect of surface structure of α-Fe2O3 on the selective catalytic reduction of NO by NH3 [J].物理化学学报,2012,28(1):184-188. |
| 21 | YANG Xingye, LI Bin, SUN Liang, et al.Effect of surface structure of α-Fe2O3 on the selective catalytic reduction of NO by NH3 [J].Acta Physico-Chimica Sinica,2012,28(1):184-188. |
| 22 | LIU Caixia, YANG Shijian, MA Lei, et al.Comparison on the performance of α-Fe2O3 and γ-Fe2O3 for selective catalytic reduction of nitrogen oxides with ammonia[J].Catalysis Letters,2013,143(7):697-704. |
| 23 | 余雅昕.铁基NH3-SCR催化剂的低温脱硝性能及抗SO2中毒机制研究[D].南京：南京大学，2020. |
| 23 | YU Yaxin.Study on the mechanism of SO2 resistance and the catalytic performance in low-temperature selective catalytic reduction of NO by NH3 over Fe-based catalysts[D].Nanjing：Nanjing University，2020. |
| 24 | YANG Weijie, REN Jianuo, ZHANG Hanwen, et al.Single-atom iron as a promising low-temperature catalyst for selective catalytic reduction of NO x with NH3：A theoretical prediction[J].Fuel,2021,302.Doi:10.1016/j.fuel.2021.121041. |
| 25 | HE Chuan, SHEN Boxiong, CHEN Jianhong, et al.Adsorption and oxidation of elemental mercury over Ce-MnO x /Ti-PILCs[J].Environmental Science & Technology,2014,48(14):7891-7898. |
| 26 | ZHOU Jue, GUO Ruitang, ZHANG Xinfu, et al.Cerium oxide-based catalysts for low-temperature selective catalytic reduction of NO x with NH3：A review[J].Energy & Fuels,2021,35(4):2981-2998. |
| 27 | SHAN Ye, LIU Yangxian, LI Ying, et al.A review on application of cerium-based oxides in gaseous pollutant purification[J].Separation and Purification Technology,2020,250.Doi:10.1016/j.seppur.2020.117181. |
| 28 | PEYROVI P, GILLOT S, DACQUIN J P, et al.The activity of CeVO4-based catalysts for ammonia-SCR：Impact of surface cerium enrichment[J].Catalysis Letters,2021,151(4):1003-1012. |
| 29 | CHEN Chuanmin, CAO Yue, LIU Songtao, et al.Review on the latest developments in modified vanadium-titanium-based SCR catalysts[J].Chinese Journal of Catalysis,2018,39(8):1347-1365. |
| 30 | LIU Caixia, CHEN Liang, LI Junhua, et al.Enhancement of activity and sulfur resistance of CeO2 supported on TiO2-SiO2 for the selective catalytic reduction of NO by NH3 [J].Environmental Science & Technology,2012,46(11):6182-6189. |
| 31 | Jinsun CHA, CHOI J C, KO J H, et al.The low-temperature SCR of NO over rice straw and sewage sludge derived char[J].Chemical Engineering Journal,2010,156(2):321-327. |
| 32 | 汪怀建,涂翔,黄碧纯,等.生物炭应用于低温NH3-SCR脱硝催化剂的研究进展[J].江西农业大学学报,2021,43(2):445-458. |
| 32 | WANG Huaijian, TU Xiang, HUANG Bichun, et al.Review on application of biochar to denitrification catalysts for low-temperature NH3-SCR[J].Acta Agriculturae Universitatis Jiangxiensis,2021,43(2):445-458. |
| 33 | IWAMOTO M, FURUKAWA H, MINE Y, et al.Copper（Ⅱ） ion-exchanged ZSM-5 zeolites as highly active catalysts for direct and continuous decomposition of nitrogen monoxide[J].Journal of the Chemical Society，Chemical Communications,1986(16).Doi:10.1039/C39860001272. |
| 34 | PEREIRA M V L, NICOLLE A, BERTHOUT D.Hydrothermal aging effects on Cu-zeolite NH3-SCR catalyst[J].Catalysis Today,2015,258: 424-431. |
| 35 | SHWAN S, JANSSON J, OLSSON L, et al.Deactivation mechanisms of iron-exchanged zeolites for NH3-SCR applications[J].Catalysis Today,2015,258: 432-440. |
| 36 | 章凌,段宏昌,谭争国,等.用于柴油车尾气消除反应（NH3-SCR）的八元环沸石分子筛研究进展[J].高等学校化学学报,2020,41(1):19-27. |
| 36 | ZHANG Ling, DUAN Hongchang, TAN Zhengguo, et al.Recent advances in the preparation of 8MR zeolites for the selective catalytic reduction of NO x （NH3-SCR） in diesel engines[J].Chemical Journal of Chinese Universities,2020,41(1):19-27. |
| 37 | 王彬宇,李莉,李菁,等.用工业固体废料合成沸石分子筛的研究进展[J].高等学校化学学报,2021,42(1):40-59. |
| 37 | WANG Binyu, LI Li, LI Jing, et al.Recent progresses on the synthesis of zeolites from the industrial solid wastes[J].Chemical Journal of Chinese Universities,2021,42(1):40-59. |
| 38 | GELVES J F, DORKIS L, MáRQUEZ M A, et al.Activity of an iron colombian natural zeolite as potential geo-catalyst for NH3-SCR of NO x [J].Catalysis Today,2019,320: 112-122. |
| 39 | FENG Xi, LIN Qingjin, CAO Yi, et al.Neodymium promotion on the low-temperature hydrothermal stability of a Cu/SAPO-34 NH3-SCR monolith catalyst[J].Journal of the Taiwan Institute of Chemical Engineers,2017,80: 805-812. |
| 40 | LISI L, CIMINO S.Poisoning of SCR catalysts by alkali and alkaline earth metals[J].Catalysts,2020,10(12).Doi:10.3390/catal10121475. |
| 41 | LIU Chang, SHI Jianwen, GAO Chen, et al.Manganese oxide-based catalysts for low-temperature selective catalytic reduction of NO x with NH3：A review[J].Applied Catalysis A：General,2016,522: 54-69. |
| 42 | SHEN Boxiong, LIU Ting.Deactivation of MnO x -CeO x /ACF catalysts for low-temperature NH3-SCR in the presence of SO2 [J].Acta Physico-Chimica Sinica,2010,26(11):3009-3016. |
| 43 | WANG Chizhong, YANG Shijian, CHANG Huazhen, et al.Dispersion of tungsten oxide on SCR performance of V2O5WO3/TiO2：Acidity，surface species and catalytic activity[J].Chemical Engineering Journal,2013,225: 520-527. |
| 44 | KIJLSTRA W S, BRANDS D S, POELS E K, et al.Kinetics of the selective catalytic reduction of NO with NH3 over MnO x /Al2O3 catalysts at low temperature[J].Catalysis Today,1999,50(1):133-140. |
| 45 | ZHAO Ziwei, LI Erwei, QIN Yu, et al.Density functional theory （DFT） studies of vanadium-titanium based selective catalytic reduction（SCR） catalysts[J].Journal of Environmental Sciences （China）,2020,90: 119-137. |
| 46 | 郭梓阳,霍旺晨,张育新,等.锰基低温NH3-SCR脱硝催化剂的研究概述[J].材料导报,2021,35(13):13085-13099. |
| 46 | GUO Ziyang, HUO Wangchen, ZHANG Yuxin, et al.A review of Mn-based low temperature NH3-SCR denitration catalyst[J].Materials Reports,2021,35(13):13085-13099. |
| 47 | JIANG Ye, LAI Chengzhen, LI Qingyi, et al.The poisoning effect of KCl and K2O on CeO2-TiO2 catalyst for selective catalytic reduction of NO with NH3 [J].Fuel,2020,280.Doi:10.1016/j.fuel.2020.118638. |
| 48 | JIANG Ye, LIU Tianyu, LAI Chengzhen, et al.Deactivation of CeO2-TiO2 catalyst by K2SO4 for NH3-SCR：An experimental and DFT study[J].Applied Surface Science,2021,547.Doi:10.1016/j.apsusc.2021.149196. |
| 49 | TANG Xiaolong, SHI Yiran, GAO Fengyu, et al.Promotional role of Mo on Ce0.3FeO x catalyst towards enhanced NH3-SCR catalytic performance and SO2 resistance[J].Chemical Engineering Journal,2020,398.Doi:10.1016/j.cej.2020.125619. |
| 50 | PHULE A D, CHOI J H, KIM J H.High performance of catalytic sheet filters of V2O5-WO3/TiO2 for NO x reduction[J].Environmental Science and Pollution Research International,2021,28(26):34009-34016. |
| 51 | ZHANG Xianlong, LV Shuangshuang, ZHANG Xincheng, et al.Improvement of the activity and SO2 tolerance of Sb-modified Mn/PG catalysts for NH3-SCR at a low temperature[J].Journal of Environmental Sciences,2021,101: 1-15. |
| 52 | XIONG Shangchao, PENG Yue, WANG Dong, et al.The role of the Cu dopant on a Mn3O4 spinel SCR catalyst：Improvement of low-temperature activity and sulfur resistance[J].Chemical Engineering Journal,2020,387 .Doi:10.1016/j.cej.2020.124090. |
| 53 | 李锋,金保升,刘涛,范红梅.以工业级TiO2为载体负载不同助催化剂V2O5基脱氮催化剂的性能[J].环境化学,2005,24(4):374-378. |
| 53 | LI Feng, JIN Baosheng, LIU Tao, et al.Study of deNO x behavior of V2O5-based catalyst with different catalyst promoters supported on commercial anatase TiO2 [J].Environmental Chemistry,2005,24(4):374-378. |
| 54 | 朱崇兵,金保升,李锋,等.V2O5-WO3/TiO2基催化剂SCR法脱硝试验研究[J].华东电力,2007,35(6):18-22. |
| 54 | ZHU Chongbing, JIN Baosheng, LI Feng, et al.Experiment study on SCR DeNO x behavior of V2O5-WO3/TiO2 catalysts[J].East China Electric Power,2007,35(6):18-22. |
/
| 〈 |
|
〉 |