湿法解毒铁铬渣作混凝土掺合料的性能研究

  • 王缘 ,
  • 王智 ,
  • 秦洪一
展开
  • 重庆大学材料科学与工程学院,重庆 400030
王缘(1995— ),男,在读博士研究生,主要从事固废综合利用;E-mail: wangyuan9558@163.com

收稿日期: 2021-05-18

  网络出版日期: 2022-03-18

Study on properties of wet detoxification Fe-Cr slag as concrete admixture

  • Yuan WANG ,
  • Zhi WANG ,
  • Hongyi QIN
Expand
  • College of Materials Science and Engineering,Chongqing University,Chongqing 400030,China

Received date: 2021-05-18

  Online published: 2022-03-18

摘要

铁铬渣是以铬铁矿为原料生产金属铬和铬盐后产生的工业废渣。经硫酸亚铁湿法解毒的铁铬渣仍然具有一定的火山灰活性,可作混凝土矿物掺合料使用。然而由于湿法解毒铁铬渣含有水溶性铬(Ⅵ),影响了其建材化资源利用。研究了湿法解毒铁铬渣的粒径分布、火山灰活性;以湿法解毒铁铬渣作为矿物掺合料代替粉煤灰用于C30混凝土,考察了混凝土的工作性能、力学性能和水溶性铬(Ⅵ)的浸出量。结果表明:湿法解毒铁铬渣的粒径主要分布在1~20 μm,28 d活性指数达到68%;当湿法解毒铁铬渣取代20%(以质量分数计)粉煤灰时,混凝土坍落度增加了38.2%,7 d和28 d强度分别增加了7%和6%;混凝土浸出液中水溶性铬(Ⅵ)的浓度,根据标准的不同其要求也不同。湿法解毒铁铬渣有作为矿物掺合料的可能性,但是需要考虑其水溶性铬(Ⅵ)的浸出量,以确保混凝土的安全使用。

本文引用格式

王缘 , 王智 , 秦洪一 . 湿法解毒铁铬渣作混凝土掺合料的性能研究[J]. 无机盐工业, 2022 , 54(3) : 87 -90 . DOI: 10.19964/j.issn.1006-4990.2021-0327

Abstract

Fe-Cr slag is an industrial waste produced after using chromite as raw material to produce metal chromium and chromium salts.After wet detoxification by FeSO4,the Fe-Cr slag still has certain volcanic ash activity,which can be used as concrete mineral admixture.However,the water-soluble Cr(Ⅵ) in wet detoxification of Fe-Cr slag affects the utilization of building materials resources.The particle size distribution and volcanic ash activity of the wet detoxification Fe-Cr slag were studied.The wet detoxification Fe-Cr slag was used as mineral admixture instead of fly ash in C30 concrete.The working properties,mechanical properties and leaching amount of water-soluble Cr(Ⅵ) of concrete were investigated.The results sho-wed that the particle size of the wet detoxification Fe-Cr slag was mainly distributed in the range of 1~20 μm,and the activity index of 28 d reached 68%.When the fly ash was replaced by 20% by the wet detoxification Fe-Cr slag,the slump of concrete increased by 38.2%,and the strength of concrete at 7 d and 28 d increased by 7% and 6%,respectively.The amount of water soluble Cr(Ⅵ) was different according to the different standard.Wet detoxification Fe-Cr slag may be used as mineral admix-ture,but the leaching of water-soluble Cr(Ⅵ) should be considered to ensure the safe use of concrete.

参考文献

[1] 韩露, 谭建红, 刘思琪. 铬渣的环境危害及其治理技术研究[J]. 广州化工, 2016, 44(6):10-11,24.
[2] 庆朋辉, 董玉明, 王兴润, 等. 铬铁矿无钙焙烧铬渣的深度提铬与无害化处理[J]. 无机盐工业, 2020, 52(6):63-67,104.
[3] 周斌, 石燕, 邵煜锟, 等. 湿法解毒技术对铬渣污染土壤的修复效果研究[J]. 中国环保产业, 2021(1):53-57.
[4] 史建斌. 铬渣无害化处理方案优化探讨[J]. 无机盐工业, 2013, 45(6):4-7.
[5] 陈窈君, 李来顺, 吕正勇, 等. 湿法解毒还原工艺对铬渣中Cr(Ⅵ)的治理特性[J]. 环境工程, 2020, 38(6):67-74.
[6] 张大威, 李霞, 纪柱. 铬铁矿无钙焙烧工艺参数控制研究[J]. 无机盐工业, 2012, 44(6):37-39.
[7] 原金海, 倪艳兵, 李娟娟. 铬渣解毒及其综合利用技术研究进展[J]. 重庆科技学院学报:自然科学版, 2008(6):59-62,71.
[8] 刘曦. 铬渣湿法解毒工艺研究[J]. 化工管理, 2014(33):163-164.
[9] 吕辉. 铬渣作水泥原料及混合材的试验研究[J]. 水泥, 2005(11):8-10.
文章导航

/