Study on preparation of hexagonal plates of magnesium hydroxide by light-burned magnesium oxide
Received date: 2021-03-16
Online published: 2022-03-14
以盐湖产不同粒径轻烧氧化镁为原料,通过水化水热法制备六角片状氢氧化镁。考察了不同的反应温度、反应时间、搅拌速度和固液比对氧化镁水化率、制得氢氧化镁形貌、粒径的影响。采用X射线衍射仪、扫描电子显微镜、激光粒度仪等对所制得的氢氧化镁颗粒的物相、形貌和粒度进行了分析,同时把不同原料所得氢氧化镁用在聚乙烯（PE）中检测其阻燃性能。结果表明通过控制反应温度、反应时间、搅拌速度和固液比,氧化镁原粉的水化率可以达到95%,氧化镁细磨粉的水化率可达到100%,得到的氢氧化镁均呈现六角片状,但粒径尺寸存在差异。用在PE中,细粒径的氢氧化镁分散性更好,阻燃效果更明显。
孔会民 , 邹来禧 , 刘远 , 曹雨微 , 林彦军 , 罗仙平 . 以轻烧氧化镁制备六角片状氢氧化镁的研究[J]. 无机盐工业, 2022 , 54(1) : 39 -44 . DOI: 10.19964/j.issn.1006-4990.2021-0154
Hexagonal plates of magnesium hydroxide was prepared from salt lake light-burned magnesia with different grain size by hydration-hydrothermal method.The influence of reaction temperature,reaction time,stirring rate and solid-liquid ratio on the conversion rate of magnesia,the morphology and particle size of magnesium hydroxide was investigated systematically. The phase,morphology and particle size of magnesium hydroxide were investigated by X-ray diffraction（XRD）,scanning electronic microscope（SEM）,and laser particle size analyzer（LPSA） respectively.Meanwhile,magnesium hydroxide from di-fferent raw materials was added in PE to test its flame retardancy.The results showed that by controlling the reaction tempera-ture,reaction time,stirring speed and solid-liquid ratio,the hydration rate of magnesium oxide raw powder could reach 95%,the hydration rate of magnesium oxide fine grinding powder could reach 100%,and the obtained magnesium hydroxide was both hexagonal,but the particle size was different.When it was used in PE,fine-grained magnesium hydroxide had better dispersion and more obvious flame retardant performance.
| [1] | 孙淑英, 宋兴福, 张登科, 等. 废弃水氯镁石反应结晶制备高纯氢氧化镁[J]. 环境科学与技术, 2010, 33(12F):298-300. |
| [2] | 曹雨微, 逯登琴, 宋学文, 等. 新型镁系阻燃材料制备工艺及应用研究现状[J]. 盐科学与化工, 2019, 48(10):8-14. |
| [3] | 罗仙平, 李建康, 徐徽, 等. 电熔镁砂制备工艺及熔炼过程[J]. 盐业与化工, 2016, 45(8):8-13. |
| [4] | 李陇岗, 钟辉, 杨建元. 盐湖水氯镁石制备高纯镁砂的研究进展[J]. 盐湖研究, 2004, 12(1):57-61. |
| [5] | 徐徽, 程俊峰, 李贵, 等. 水氯镁石制备硅钢级氧化镁[J]. 材料导报, 2013, 27(8):104-107. |
| [6] | PILARSKA A A, KLAPISZEWSKI L, JESIONOWSKI T. Recent de-velopment in the synjournal,modification and application of Mg(OH)2 and MgO[J]. Powder Technology, 2017, 319:373-407. |
| [7] | 韩以群, 王朝乾. 氢氧化镁生产及其废液在烟气脱硫中的应用研究[J]. 盐科学与化工, 2017, 46(4):35-37. |
| [8] | 郭如新. 氢氧化镁在工业废水处理中应用研究进展[J]. 精细与专用化学品, 2010, 18(4):42-47. |
| [9] | 潘晓鸿, 杨兆元, 李东哲, 等. 纳米氢氧化镁对抗菌类药物的增效作用[J]. 基因组学与应用生物学, 2016, 35(12):3249-3254. |
| [10] | DONG C, CAIRNEY J, SUN Q, et al. Investigation of Mg(OH)2 nano-particles as an antibacterial agent[J]. Journal of Nanoparticle Re-search, 2010, 12(10):2101-2109. |
| [11] | DONG C, HE G, ZHENG W, et al. Study on antibacterial mechanism of Mg(OH)2 nanoparticles[J]. Materials Letters, 2014, 134(11):286-289. |
| [12] | PILARSKA A, BULA K, MYSZKA K, et al. Functional polypro-pylene composites filled with ultra-fine magnesium hydroxide[J]. Open Chemistry, 2015, 13(9):161-171. |
| [13] | LI H, LIU S, ZHAO J, et al. Removal of reactive dyes from waste water assisted with kaolin clay by magnesium hydroxide coagula-tion process[J]. Colloids and Surfaces A-Physicochemical and Eng-ineering Aspects, 2016, 494:222-227. |
| [14] | LIU S. Flame retardant and mechanical properties of polyethylene/magnesium hydroxide/montmorillonite nanocomposites[J]. Journal of Industrial and Engineering Chemistry, 2014, 20(4):2401-2408. |
| [15] | GUL R, ISLAM A, YASIN T, et al. Flame-retardant synergism of sepiolite and magnesium hydroxide in a linear low-density polye-thylene composite[J]. Journal of Applied Polymer Science, 2011, 121(5):2772-2777. |
| [16] | SUIHKONEN R, NEVALAINEN K, ORELL O, et al. Performance of epoxy filled with nano-and micro-sized magnesium hydroxide[J]. Journal of Materials Science, 2012, 47(9):1480-1488. |
| [17] | 刘志启, 李丽娟, 曾忠民, 等. 用水氯镁石制备单分散六角片状氢氧化镁[J]. 材料科学与工艺, 2011, 19(4):138-144. |
| [18] | LIU L, HU J, ZHUO J, et al. Synergistic flame retardant effects bet-ween hollow glass microspheres and magnesium hydroxide in ethy-lene-vinyl acetate composites[J]. Polymer Degradation and Stabi-lity, 2014, 104(6):87-94. |
| [19] | CHEN X, JIE Y, GUO S, et al. Surface modification of magnesium hydroxide and its application in flame retardant polypropylene co-mposites[J]. Journal of Materials Science, 2009, 44(5):1324-1332. |
| [20] | GENOVESE A, SHANKS R A. Structural and thermal interpreta-tion of the synergy and interactions between the fire retardants magnesium hydroxide and zinc borate[J]. Polymer Degradation and Stability, 2007, 92(1):2-13. |
| [21] | CHEN D, ZHENG Q, LIU F, et al. Flame-retardant polypropylene composites based on magnesium hydroxide modified by phospho-rous-containing polymers[J]. Journal of Thermoplastic Composite Materials, 2009, 23(2):175-192. |
| [22] | 徐嘉欣, 颜粉鸽, 黄建翠, 等. 高分散型六角片状氢氧化镁的制备与表征[J]. 盐科学与化工, 2018, 47(3):14-21. |
| [23] | 宋雪雪, 李丽娟, 姬连敏, 等. 纳米及微米级六角片状氢氧化镁的制备[J]. 盐湖研究, 2018, 26(2):66-74. |
| [24] | 赵卓雅, 李祥高, 王世荣, 等. 六角片状氢氧化镁(001)晶面优先生长条件的研究[J]. 人工晶体学报, 2014, 43(7):1611-1619. |
| [25] | 吴易梅, 孙玉柱, 路贵民, 等. 结晶-水热法制备六角片状氢氧化镁[J]. 高等化学工程学报, 2019, 32(2):425-434. |
| [26] | CHEN Y, ZHOU T, FANG H, et al. A novel preparation of nano-sized hexagonal Mg(OH)2 as a flame retardant[J]. China Particuo-logy, 2016, 24(1):177-182. |
| [27] | FANG H, ZHOU T, CHEN X, et al. Controlled preparation and cha-racterization of nano-sized hexagonal Mg(OH)2 flame retardant[J]. China Particuology, 2014, 14(3):51-56. |
| [28] | JIN D, GU X, YU X, et al. Hydrothermal synjournal and characteri-zation of hexagonal Mg(OH)2 nano-flake as a flame retardant[J]. Materials Chemistry & Physics, 2008, 112(3):962-965. |
| [29] | 汪艳, 王伟, 张俊, 等. 轻烧镁粉制备超细片状氢氧化镁[J]. 武汉工程大学学报, 2013, 35(1):41-45. |
| [30] | 孙晓君, 丁珂, 仇龙, 等. 以轻烧粉制备六方片状氢氧化镁[J]. 硅酸盐学报, 2019, 47(4):530-536. |
/
| 〈 |
|
〉 |