复合外加剂改性盐石膏的研究

  • 李志新 ,
  • 徐开东 ,
  • 周浩 ,
  • 王继娜 ,
  • 张建武 ,
  • 郭高巍
展开
  • 1.河南城建学院材料与化工学院,河南省城市固废综合处置与生态利用协同创新中心,河南平顶山 467036
    2.浙江红狮控股集团有限公司
李志新(1989— ),男,博士,讲师,主要从事固废综合利用方面的研究;E-mail:li.zhixin1989@163.com

收稿日期: 2020-05-13

  网络出版日期: 2020-12-01

基金资助

河南省高等学校重点科研项目(20A560005);河南省城市固废综合处置与生态利用协同创新中心开放课题资助;河南城建学院青年骨干教师资助项目(YCJQNGGJS201908);河南省科技厅科技攻关计划项目(182102310928)

Study on composite admixtures modified salt gypsum

  • Zhixin Li ,
  • Kaidong Xu ,
  • Hao Zhou ,
  • Jina Wang ,
  • Jianwu Zhang ,
  • Gaowei Guo
Expand
  • 1. Henan Provincial Solid Waste Comprehensive Disposal and Ecological Utilization Collaborative Innovation Center Open Project Funded Project,School of Material and Chemical Engineering,Henan University of Urban Construction,Pingdingshan 467036
    2. Zhejiang Hongshi Holding Group Co.,Ltd.

Received date: 2020-05-13

  Online published: 2020-12-01

摘要

盐石膏的主要成分为无水硫酸钙,其活性差、凝结硬化慢、强度低,需要添加活性剂来激发盐石膏的活性。通过复合外加剂对盐石膏加以改性,并通过XRD和SEM对其作用机理做了分析。结果表明,单掺脱硫石膏和建筑石膏均能缩短盐石膏的凝结时间,建筑石膏的效果较好,但掺量不宜过高。复掺建筑石膏和缓凝剂时,两者比例要控制得当,适宜的建筑石膏和缓凝剂掺量分别为50%和0.10%~0.12%(质量分数)。分析可知,大掺量建筑石膏会增加盐石膏硬化体中二水相和针棒状晶体的含量;缓凝剂掺量的增加,会降低盐石膏硬化体中二水相的含量,棱形晶体增多,从而降低了盐石膏的强度。

本文引用格式

李志新 , 徐开东 , 周浩 , 王继娜 , 张建武 , 郭高巍 . 复合外加剂改性盐石膏的研究[J]. 无机盐工业, 2020 , 52(11) : 75 -78 . DOI: 10.11962/1006-4990.2019-0635

Abstract

Salt gypsum is a waste residue produced in the salt industry.The main component of salt-gypsum is anhydrous cal-cium sulfate.It is necessary to add active agent to stimulate the activity of salt gypsum for its poor activity,slow setting and hardening rate,and low strength.The salt gypsum is modified by composite admixtures and its action mechanism is analyzed by XRD and SEM.The results showed that the single-doped flue gas desulfurization(FGD) gypsum or plaster of Paris could both shorten the setting time and increase the strength of salt gypsum,and the effect of plaster of Paris was better,but the dosage should not be too high.The addition of retarder could retard the setting time and decrease the strength of plaster,thus the amount of retarder should be appropriate as well.When the plaster of Paris and retarder were mixed,the ratio of them should be properly controlled and the suitable dosages of plaster of Paris and retarder were 50%(mass fraction,same as blow) and 0.10%~0.12%,respectively.The analysis showed that the high content of plaster of Paris will increase the amount of the dihydrate phase and the needle and bar crystals in the hardened salt gypsum;the increase of the retarder content will reduce the amount of the dihydrate phase in the hardened body of the salt gypsum,and the prismatic crystals will increase as well,thus reducing the strength of salt gypsum.

参考文献

[1] 周秀云, 陈柳扬, 陈侠, 等. 盐石膏制备硫酸钙晶须工艺研究[J]. 盐业与化工, 2012,41(7):22-25.
[2] 李贵素. 盐石膏制作石膏砖[J].中国井矿盐, 1981(1):40.
[3] 王胜春, 唐贺丰, 李天祥. 添加海盐石膏对水泥增强研究及预测模型[J]. 非金属矿, 2007,30(1):29-31,51.
[4] 王胜春, 周会珠, 田永淑, 等. 盐石膏作硅酸盐水泥添加剂的研究[J]. 无机盐工业, 2007,39(6):44-46.
[5] 于水军, 魏月贝, 杨岱霖. 基于正交试验的粉煤灰石膏基自流平砂浆性能研究[J]. 硅酸盐通报, 2018,37(10):3217-3222.
[6] 陈柳扬. 盐石膏制备硫酸钙晶须工艺研究[D]. 天津:天津科技大学, 2012.
[7] 陈侠, 李瑞宁, 陈丽芳, 等. 激发剂作用下的盐石膏废渣的水化过程[J]. 环境化学, 2011,30(10):1725-1730.
[8] 汪家铭. 河南舞阳建设12万吨/年盐石膏综合利用项目[J]. 四川化工, 2013,16(5):53.
[9] 贾晓华, 张永松, 黄伟, 等. 盐石膏转晶与分离中试研究[J]. 盐科学与化工, 2017,46(6):50-52.
[10] 张金良, 吴向东, 符勇. 钢渣-矿渣基胶凝材料特性研究[J]. 能源与环保, 2019,41(6):66-68.
[11] 袁翠玉. 钙对重金属废渣水热硫化工艺的影响研究[D]. 长沙:中南大学, 2013.
文章导航

/