膜集成技术处理氯化法钛白后处理废水的研究

  • 彭文博 ,
  • 恽建军 ,
  • 丁邦超 ,
  • 白祖国 ,
  • 肖维溢 ,
  • 王肖虎
展开
  • 江苏久吾高科技股份有限公司,江苏南京 211808
彭文博(1981— ),男,博士,高级工程师,研究方向为膜制备与应用,发表学术论文20余篇,申请专利160余项;E-mail: pengwenbo@jiuwu.com

收稿日期: 2020-01-11

  网络出版日期: 2020-06-12

Study on membrane integration technology in treatment of wastewater from chlorinated titanium dioxide

  • Wenbo Peng ,
  • Jianjun Yun ,
  • Bangchao Ding ,
  • Zuguo Bai ,
  • Weiyi Xiao ,
  • Xiaohu Wang
Expand
  • Jiangsu Jiuwu Hi-Tech Corporation Limited,Nanjing 211808,China

Received date: 2020-01-11

  Online published: 2020-06-12

摘要

氯化法钛白无机包膜处理工序会产生大量中性废水,其中包含少量钛白粉和水溶性盐,现阶段企业多以外排为主。采用膜集成(陶瓷膜+反渗透膜+纳滤膜)技术对氯化法钛白后处理废水的处理进行研究。将氯化法钛白后处理废水用陶瓷膜过滤,分离回收二氧化钛;将陶瓷膜清液用反渗透膜浓缩,清水回收利用;将反渗透浓液用纳滤膜分离硫酸钠和氯化钠。结果表明:利用陶瓷膜处理氯化法钛白后处理废水,平均通量为650 L/(m 2·h),浓液中钛白粉质量浓度达到90 g/L以上,清液中钛白粉质量浓度低于0.001 g/L;使用反渗透膜截留清液中的硫酸钠和氯化钠,硫酸钠和氯化钠的截留率为99.5%,浓水中的盐质量分数达到4%以上;浓水中的硫酸钠和氯化钠通过纳滤膜分离,纳滤膜对硫酸钠的截留率为97%,硫酸钠质量分数达到14%以上。

本文引用格式

彭文博 , 恽建军 , 丁邦超 , 白祖国 , 肖维溢 , 王肖虎 . 膜集成技术处理氯化法钛白后处理废水的研究[J]. 无机盐工业, 2020 , 52(6) : 76 -79 . DOI: 10.11962/1006-4990.2019-0369

Abstract

A large number of neutral wastewater will be produced in the process of chlorinated titanium dioxide by inorganic coating treatment technology,which contains a small amount of titanium dioxide and water-soluble salts.At present,the titanium dioxide and water-soluble salts are discharged outside by most of the enterprises.The membrane integration(ceramic membrane+reverse osmosis membrane+nanofiltration membrane) treatment process was used to study the chlorination titanium dioxide post-treatment wastewater.TiO2 was separated and recovered by ceramic membrane filtration;the clear liquid of ceramic membrane was concentrated by reverse osmosis membrane and the clean water was recycled;the concentrated liquid of reverse osmosis was separated by nanofiltration membrane to separate sodium sulfate and sodium chloride.The results showed that the average flux of ceramic membrane was 650 L/(m 2·h),the mass concentration of titanium dioxide in the concentrate was 90 g/L,and mass concentration of titanium dioxide in permeate was less than 0.001 g/L.With the filtration of reverse osmosis membrane,retention rate of sodium sulfate and sodium chloride could reached above 99.5% and the mass fraction of salt in concentrated water was above 4%.Sodium sulfate and sodium chloride in concentrated water were separated by nanofiltration membrane.With the filtration of nanofiltration membrane,retention rate of sodium sulfate could reached 97%.Sodium sulfate concentration can reach more than 14%.

参考文献

[1] 江书安, 刘建良, 李雪刚 . 中国氯化钛白现状及发展趋势[J]. 有色金属设计, 2016,43(3):60-64.
[2] 马晨璐 . 龙蟒佰利子公司拟投建20万吨/年氯化法钛白粉项目[J].中国钛业, 2018(1):50-51.
[3] 《功能材料信息》编辑部. 加快氯化法钛白粉产业化进程[J]. 功能材料信息, 2016,13(4):24-25.
[4] 刘建良 . 中国氯化钛白现状及发展趋势[J].中国金属通报, 2016(8):58-61.
[5] 范基隆, 丁复兴 . 提高钛白粉耐候性的工艺研究[J]. 化工设计通讯, 2019,45(7):117-118.
[6] 马磊 . 氯化法钛白粉表面包膜关键因素研究[D]. 昆明:云南大学, 2016.
[7] 徐高栋 . 中国钛白行业刮起“绿色飓风”[J]. 精细化工原料及中间体, 2010(2):12-16.
[8] 徐高栋 . 中国钛白产业环保现状与节能减排策略[J]. 新材料产业, 2010(1):37-40.
[9] 王志高, 肖维溢, 丁邦超 , 等. 膜分离集成技术处理硫酸法钛白粉酸性废水的研究[J]. 无机盐工业, 2018,50(4):53-55.
[10] 赵宜江, 李红, 徐南平 , 等. 陶瓷微滤膜回收偏钛酸过程中膜清洗的研究[J]. 膜科学与技术, 1998,18(4):10-14.
[11] 王怀林, 云金明, 吴欢 , 等. 膜分离技术在脱硫废水零排放处理中的应用研究[J]. 膜科学与技术, 2018,38(6):105-110.
[12] 李具康, 代佼 . 硫酸法钛白粉“三废”治理与利用的研究进展[J]. 环境科学导刊, 2014,33(4):63-66.
[13] 王帅, 郭慧枝, 袁江龙 , 等. 煤化工高盐废水的纳滤膜分盐效果分析[J]. 工业用水与废水, 2019,50(3):35-40.
文章导航

/