陶瓷超滤膜用于盐湖卤水提锂合格液的中试研究

  • 李新望 ,
  • 谷晓娟 ,
  • 左大海 ,
  • 杨树雄 ,
  • 彭康明
展开
  • 1.纳诺斯通水务技术(上海)有限公司,上海 200041
    2.极膜环境科技(上海)有限公司
李新望(1980— ),男,硕士,工程师,研究方向为水处理新材料及其工艺应用;E-mail: leexwfly@hotmail.com。

收稿日期: 2019-10-22

  网络出版日期: 2020-04-22

Pilot study of ceramic ultrafiltration membrane for qualified lithium-extraction solution from salt lake brine

  • Xinwang Li ,
  • Xiaojuan Gu ,
  • Dahai Zuo ,
  • Shuxiong Yang ,
  • Kangming Peng
Expand
  • 1.Nanostone Water Technology(Shanghai)Co. Ltd.,Shanghai 200041,China
    2.XMEM Environmental Technology(Shanghai)Co. Ltd.

Received date: 2019-10-22

  Online published: 2020-04-22

摘要

为解决纳滤膜用于盐湖卤水镁锂分离中长时间运行后出现通量下降、膜污染和分离效率下降的问题,开展了将陶瓷超滤膜作为纳滤预处理措施用于盐湖卤水提锂合格液的中试研究。中试设在吸附提锂车间,进水为提锂工序中的合格液。结果表明,在冬天低温环境合格液浊度<50 NTU的条件下,以及在合格液浊度上升至50~170 NTU的极端进水水质条件下,陶瓷超滤膜均可在300 L/(m 2·h)的测试通量下稳定运行,过滤时间为30~50 min/周期。产水浊度稳定<0.1 NTU,优于后续纳滤系统进水要求。

本文引用格式

李新望 , 谷晓娟 , 左大海 , 杨树雄 , 彭康明 . 陶瓷超滤膜用于盐湖卤水提锂合格液的中试研究[J]. 无机盐工业, 2020 , 52(4) : 61 -64 . DOI: 10.11962/1006-4990.2019-0295

Abstract

To solve the problem of flux depression,membrane fouling and separation efficiency decline of nanofiltration mem-brane after long term operation in the separation of Mg 2+/Li + from salt lake brine,the pilot-scale study using ceramic ultrafil-tration membrane as a nanofiltration pretreatment measure for qualified lithium extraction solution from salt lake brine was conducted.The pilot facility was set in the lithium extraction workshop and the qualified solution from lithium extraction pro-cess was used as influent.The results showed that,the ceramic ultrafiltration membrane continuously and stably ran under the flux of 300 L/(m 2·h) both under the normal water quality conditions of influent turbidity below 50 NTU at low temperature in winter and under the condition of extreme influent turbidity of qualified liquid rising to 50~170 NTU,the filtration time was in the range of 30~50 min/cycle.The permeate turbidity was stably below 0.1 NTU,which was better than the influent quality re-quirement of subsequent nanofiltration.

参考文献

[1] 余疆江, 郑绵平, 伍倩 . 富锂盐湖提锂工艺研究进展[J]. 化工进展, 2013,32(1):13-21.
[2] 高峰, 郑绵平, 乜贞 , 等. 盐湖卤水锂资源及其开发进展[J]. 地球学报, 2011,32(4):483-492.
[3] 张海珍, 丁浩, 许振良 . 面向盐湖卤水和海水的锂资源膜法提锂现状与进展[J]. 水处理技术, 2017,43(12):1-7.
[4] 冯跃华 . 我国盐湖卤水提锂工程化现状及存在问题[J]. 武汉工程大学学报, 2013,35(5):9-14.
[5] 刘东帆, 孙淑英, 于建国 . 盐湖卤水提锂技术研究与发展[J]. 化工学报, 2018,69(1):141-155.
[6] 张秀峰, 谭秀民, 张利珍 . 纳滤膜分离技术应用于盐湖卤水提锂的研究进展[J]. 无机盐工业, 2017,49(1):1-5.
[7] 徐萍, 钱晓明, 郭昌盛 , 等. 用于盐湖卤水镁锂分离的纳滤技术研究进展[J]. 材料导报, 2019,33(2):410-417.
[8] 成琪, 关云山 . 高镁锂比卤水的纳滤膜分离性能研究[J]. 无机盐工业, 2019,51(2):35-39.
[9] 付江涛, 王黎, 李新望 , 等. CM大表面积块片式陶瓷超滤膜在化工废水深度处理中的应用[J]. 水处理技术, 2017,43(4):86-93.
文章导航

/