激光粒度仪测定气相氧化法二氧化钛粒径的研究

  • 陈雯 ,
  • 龙翔 ,
  • 李海艳 ,
  • 杨辉 ,
  • 贾贵发 ,
  • 金娅秋
展开
  • 1. 贵研检测科技(云南)有限公司,云南昆明 650106
    2. 云南冶金新立钛业有限公司
陈雯(1984— ),女,硕士,工程师,主要从事稀贵金属材料制备及分析测试研究;E-mail:276395620@qq.com。

收稿日期: 2019-08-18

  网络出版日期: 2020-02-26

基金资助

国家重点研发计划超高纯稀有/稀贵金属检测评价技术与标准研究(2017YFB0305405)

Determination of particle size of gas phase oxided titanium dioxide by laser particle size analyzer

  • Wen Chen ,
  • Xiang Long ,
  • Haiyan Li ,
  • Hui Yang ,
  • Guifa Jia ,
  • Yaqiu Jin
Expand
  • 1. Guiyan Detection Technology(Yunnan) Co.,Ltd.,Kunming 650106,China
    2. Yunnan Metallurgical Xinli Titanium Industry Co.,Ltd.

Received date: 2019-08-18

  Online published: 2020-02-26

摘要

以中国某企业生产的气相氧化法二氧化钛为研究对象,采用马尔文激光粒度仪测定气相氧化法二氧化钛的粒径分布,研究了折射率、吸收率、遮光度对测定二氧化钛粒径分布的影响。结果表明,折射率与物料的晶体结构相关,应根据晶体结构选择合适的折射率;随着吸收率变大,残差值先变小后变大;遮光度大于20%时,平均粒径明显变小,且残差值变大。通过实验,确定了激光粒度仪测定气相氧化法二氧化钛最佳设定参数:折射率为2.71、吸收率为0.1、遮光度为10%,在上述最优条件下测定样品的平均粒径为0.329 μm,粒度分布呈较好的正态分布,通过SEM对粒径分布做表征,结果与激光粒度仪结果一致。

本文引用格式

陈雯 , 龙翔 , 李海艳 , 杨辉 , 贾贵发 , 金娅秋 . 激光粒度仪测定气相氧化法二氧化钛粒径的研究[J]. 无机盐工业, 2020 , 52(2) : 69 -71 . DOI: 10.11962/1006-4990.2019-0184

Abstract

The particle size of gas phase oxided titanium dioxide that manufactured in a China′s company was measured with a Malvern laser particle size analyzer.The effects of refractive rate,absorption rate and shading degree on the particle size of titaniumdioxide were studied.Results showed that the refractive rate was related to the crystal structure of the material.As the absorption rate increased,the residual value decreased first and then increased.When the shading degree was more than 20%,the average particle size decreased obviously and the residual value increased.The optimum parameters of the gas phase oxided titanium dioxide measured by the laser particle size analyzer were determined as follows: the refractive rate was 2.71,the absorption rate was 0.1 and the shading degree was 10%.Under the optimum conditions,the average particle size of the sample was 0.329 μm,and the particle size was normally distributed which was consistent with the results of SEM.

参考文献

[1] 杜煜 . 激光衍射法测定超细氢氧化铝粒度中分散条件的控制[J]. 理化检验:物理分册, 2013,49(1):46-49.
[2] 秦大可, 于法鹏 . Master sizer 2000粒径仪对SiO2粒径分析的影响因素研究[J]. 苏州大学学报:工科版, 2011,31(1):47-51.
[3] 汪云华, 李海艳, 张笑盈 , 等. 后处理工艺对氯化法金红石型钛白粉性能的影响研究[J]. 无机盐工业, 2015,43(3):16-18,44.
[4] 郑水林, 王彩丽 . 粉体表面改性[M]. 北京: 中国建筑工业出版社, 2011: 234.
[5] 刘培炎 . 激光粒度仪干法和湿法测试在涂料粒径分析中的应用[J]. 涂料工业, 2016,46(12):58-62.
[6] 耿淑华, 丁伟中, 郭曙强 . 激光粒度分析中颗粒折射率的确定方法[J]. 上海金属, 2014,36(2):1-4.
[7] 张国强, 赵鸣, 张丽娟, 盖国胜, 姜涛 . 激光粒度测试结果影响因素分析[J]. 中国测试, 2017,43(3):24-29.
[8] 朱晓东, 雷佳浩, 王尘茜 , 等. 热处理对铁掺杂TiO2锐钛矿-金红石相变的影响[J]. 化工新型材料, 2019,47(2):108-111.
[9] 于晓微, 付春明, 张晓波 , 等. 激光粒度仪测定锰酸锂粒度的条件试验[J]. 无机盐工业, 2014,46(6):62-63,71.
文章导航

/