磷酸活化磷尾矿制取聚合态钙镁磷肥的工艺条件研究

  • 郑建国 ,
  • 于南树 ,
  • 刘永秀 ,
  • 宋涛 ,
  • 胡兆平
展开
  • 1. 养分资源高效开发与综合利用国家重点实验室/金正大生态工程集团股份有限公司,山东临沭 276700
    2. 国家缓控释肥工程技术研究中心
    3. 贵州省磷化工清洁生产工程技术研究中心
郑建国(1990— ),男,研究员,中级工程师,硕士,主要从事磷资源高效利用及新型肥料开发相关工作;E-mail:804352453@qq.com。

收稿日期: 2019-08-17

  网络出版日期: 2020-02-26

基金资助

新型缓控释肥料与稳定肥料研制 国家重点研发计划(2017YFD0200700);非常规硝酸分解磷矿清洁生产关键技术及工程示范(2018YFC190062-5)

Study on technological conditions of polymeric calcium magnesium phosphate fertilizer from phosphoric acid activated phosphate tailings

  • Jianguo Zheng ,
  • Nanshu Yu ,
  • Yongxiu Liu ,
  • Tao Song ,
  • Zhaoping Hu
Expand
  • 1. State Key Laboratory of Nutrition Resources Integrated Utilization,Kingenta Ecological Engineering Group Co.,Ltd.,Linzhu 276700,China
    2. Engineering Technology Research Center For SCRF
    3. Guizhou Phosphorus Chemical Cleaner Production Engineering Technology Research Center

Received date: 2019-08-17

  Online published: 2020-02-26

摘要

为减少磷尾矿对环境的损害,采用高温分子间脱水聚合的方法,对利用磷尾矿合成聚合态钙镁磷肥做了研究。将磷酸和磷尾矿按照物质的量比[n(P2O5)∶n(CaO+MgO)]为1∶(1.2~1.8)进行混合反应,将反应的料浆在250~600 ℃下煅烧1~5 h得到干基的产品。产品检测结果表明,聚合态钙镁磷肥的聚合度为1~4,P2O5的聚合率在80%以上,总P2O5质量分数为50%~60%,CaO质量分数为17%左右,MgO质量分数为12%左右,产品结构为多孔隙的球状结构。该产品可以根据不同地区的需要灵活调整原料配比,以得到不同性质的产品。该研究已经在中试装置中进行试生产,正式生产车间目前正在中国贵州建设,目标产能为20万t/a。

本文引用格式

郑建国 , 于南树 , 刘永秀 , 宋涛 , 胡兆平 . 磷酸活化磷尾矿制取聚合态钙镁磷肥的工艺条件研究[J]. 无机盐工业, 2020 , 52(2) : 43 -46 . DOI: 10.11962/1006-4990.2019-0117

Abstract

In order to reduce the environmental damage caused by phosphorus tailings,the synthesis of polymeric calcium magnesium phosphate fertilizer from phosphorus tailings by high temperature intermolecular dehydration polymerization was studied.Phosphoric acid and phosphorus tailings were mixed at the amount-of-substance ratio of P2O5 to(CaO+MgO) of 1∶(1.2~1.8),and the slurry was calcined at 250~600 ℃ for 1~5 h to obtain dry-base products.The results showed that the degree of polymerization of polymeric calcium magnesium phosphate fertilizer was 1~4,the polymerization rate of P2O5 was more than 80%,the total P2O5 was 50%~60%(mass fraction),the mass fraction of CaO was about 17%,the mass fraction of MgO was about 12%,and the product structure was porous spherical structure.The product can be flexibly adjusted according to the needs of different regions to obtain products of different properties.The research has been put into trial production in pilot plant,and the formal production workshop is currently being constructed in Guizhou,China,with a target capacity of 200 kt/a.

参考文献

[1] 周倩倩, 周克清 . 磷尾矿资源综合利用现状研究[J]. 化工矿物与加工, 2018,47(9):67-70.
[2] 孙娜, 尤彩霞, 胡亚伟 , 等. 磷尾矿氨循环法分离钙镁制取氢氧化镁碳酸钙的研究[J]. 无机盐工业, 2018,50(3):57-59.
[3] 文焱炳, 张钦, 顾春光 , 等. 中低品位磷矿前处理技术的研究进展[J]. 无机盐工业, 2016,48(7):7-9.
[4] 张苏江, 易锦俊, 孔令湖 , 等. 中国磷矿资源现状及磷矿国家级实物地质资料筛选[J]. 无机盐工业, 2016,48(2):1-5,17.
[5] 胡宏, 徐德龙, 段永华 , 等. 硫磷混酸分解高镁尾矿渣制取磷镁复合肥的工艺条件研究[J]. 无机盐工业, 2012,44(2):53-55,62.
[6] 张萍花, 燕云洁, 陈建钧 , 等. 高镁钙磷尾矿酸解制纳米级碳酸钙[J]. 无机盐工业, 2019,51(3):63-66.
[7] 赵博, 陈延信, 姚艳飞 . 白云石质磷尾矿悬浮态煅烧实验研究[J]. 无机盐工业, 2013,45(5):18-20.
[8] 解田; 胡宏; 高晓明 , 等. 利用萃余酸和高镁磷尾矿渣制备磷镁复合肥料的方法:中国,102161602A[P]. 2011 -08-24.
[9] 钟矿, 陈华, 梅军 , 等. 磷酸二氢铵-尿素缩聚法制备聚磷酸铵研究[J]. 无机盐工业, 2017,39(10):30-32.
[10] 刘宜娜, 杨荣杰, 李定华 , 等. 31P核磁共振波谱表征高聚合度聚磷酸铵及其链结构 [J]. 高等学校化学学报, 2018,39(9):2080-2088.
[11] 邹志量, 胡伟, 马新刚 , 等. 固体核磁共振法测定聚磷酸铵的平均聚合度[J]. 固体火箭技术, 2012,35(4):552-554,564.
[12] 王伯通, 刘永秀, 杨蕾 . 快速测定水溶性聚磷酸铵的聚合率[J]. 磷肥与复肥, 2017,32(1):40-41.
[13] 谢少兰 . 过磷酸钙中有效磷快速测定方法研究[J]. 无机盐工业, 2010,42(6):58-60.
[14] 朱瑞仪 . 聚丙烯酰胺絮凝剂的机理和分子设计研究[J]. 当代化工研究, 2018(12):120-121.
[15] 罗敬 . 利用核磁共振法分析几种含磷物质中磷的形态与含量[D]. 长沙:湖南师范大学, 2015.
文章导航

/