doi:10.11962/1006-4990.2020-0516

摘要/Abstract

摘要：

介绍了中国无机铝铁盐行业在混凝剂应用方面60 a来的发展历程,包括一些重点混凝剂（聚硫酸铁、聚氯化铁、聚氯化铝和硫酸铝）的制备方法和工艺流程如铝灰法、铝酸钙法、氢氧化铝酸溶法、空气/氧气氧化法等;以及国内各大水厂/企业使用混凝剂的发展历史和现状。最后对铝铁盐行业的未来发展趋势进行了展望：混凝理论有待进一步发展、开发新型复合混凝剂投入实际生产应用并倡导用户避免走进“药剂纯度越高,效果越好”这一误区。

关键词: 铝盐, 铁盐, 聚氯化铝, 聚硫酸铁, 发展趋势

Abstract:

The development history of China′s aluminum-and-iron salt industry in coagulant application including the production technology and processes of some key coagulants（polymeric ferric sulfate,polymeric ferric chloride,polymeric aluminum chloride and aluminum sulfate）,such as aluminum ash method,calcium aluminate method,aluminum hydroxide acid method,air/oxygen oxidation method and so on,in past 60 years was introduced.The development history and current status of coagulants using in China′s water treatment factory and enterprise were also reviewed.Finally,an outlook on the future trends of the aluminum and iron salt industry was presented：the theory of coagulation needs to be further developed,the development of new composite coagulant needs to be applied into practical production,and there is a misunderstanding should be awared,that is“the higher the purity,the better the effect”.

Key words: aluminium salt, ferric salt, polymeric aluminium chloride, polymeric ferric sulfate, development trends

中图分类号:

李风亭,李梓彤,李杰. 中国无机铝铁盐水处理剂行业60年发展历程及未来发展趋势[J]. 无机盐工业, 2020, 52(10): 25-29.

Li Fengting,Li Zitong,Li Jie. Analysis of developing history in past 60 years and future trends of China′s inorganic aluminum and ferric salt water treatment chemicals industry[J]. Inorganic Chemicals Industry, 2020, 52(10): 25-29.

图/表 4

表1

表2

图1

表3

参考文献 24

[1]	钱易, 汤鸿霄. 水体颗粒物和难降解有机物的特性与控制技术原理[M]. 北京: 中国环境科学出版社, 2000.
[2]	汤鸿霄. 无机高分子絮凝理论与絮凝剂[M]. 北京: 中国建筑工业出版社, 2006.
[3]	常青, 王武权, 栾兆坤, 等. 聚合硅酸硫酸铝的制备、结构及性能研究[J]. 环境化学, 1999(2):3-5.
[4]	高宝玉, 王占生, 汤鸿霄. 聚硅酸铝盐混凝剂的研究进展[J]. 环境科学进展, 1998(2):3-5.
[5]	李润生. 水处理新药剂碱式氯化铝[M]. 北京: 中国建筑工业出版社, 1981.
[6]	李润生, 张莹, 唐经立, 等. 高性能聚氯化铝的研究[J]. 中国给水排水, 2010,26(23):73-75.
[7]	李润生, 俞明华, 聂祥, 等. 水处理混凝剂的评价[J]. 无机盐工业, 2017,49(5):1-4.
[8]	路光杰, 曲久辉, 汤鸿霄. 电渗析法合成高效聚合氯化铝的研究[J]. 中国环境科学, 2000(3):250-253.
[9]	Liu Z, Zhou L, Liu F, et al. Impact of Al-based coagulants on the formation of aerobic granules:Comparison between poly aluminum chloride(PAC) and aluminum sulfate(AS)[J]. Science of the Total Environment, 2019,685:74-84.
[10]	Liu Y, Zhu L. Enhanced treatment of dispersed dye-production wastewater by self-assembled organobentonite in a one-step process with poly-aluminium chloride[J]. Scientific Reports, 2017,7(1):6843.
[11]	Kasprzak P, Gonsiorczyk T, Grossart H P, et al. Restoration of a eutrophic hard-water lake by applying an optimised dosage of polyaluminium chloride(PAC)[J]. Limnologica, 2018,70:33-48.
[12]	李安, 郑雅杰, 彭映林, 等. 铝钙粉浸出渣的活化及其在锌冶炼废水处理中的应用[J]. 中国有色金属学报, 2019,29(5):1073-1082.
[13]	Zheng G, Liu C, Xia J, et al. Kinetics of aluminum extraction from aluminum ash by leaching with sulfuric acid[J]. Phosphorus Sulfur and Silicon and the Related Elements, 2020,195(7):536-543.
[14]	Brito W S, Mileo F S A L, Boca S R A A, et al. An assessment of reuse of light ash from bayer process fluidized bed boilers in geopolymer synjournal at ambient temperature[J]. Advances in Materials Science & Engineering, 2018(1):1287243.
[15]	陈辅君, 李风亭. 高盐基度聚合氯化铝的制备研究[J]. 中国给水排水, 1994,10(6):45-47.
[16]	李风亭, 周秋涛, 王颖, 等. 一种聚合氯化铝类系列盐类的干燥设备及其干燥方法:中国,108362118A[P]. 2018-08-03.
[17]	李风亭, 朱茜, 刘畅. 我国聚氯化铝的生产技术与质量控制问题[J]. 工业水处理, 2014,34(12):1-3.
[18]	Kaur G, Couperthwaite S J, Millar G J. Performance of bauxite refinery residues for treating acid mine drainage[J]. Journal of Water Process Engineering, 2018,26:28-37.
[19]	李风亭. 我国混凝剂聚合硫酸铁的技术发展现状[J]. 工业水处理, 2002,22(1):5-8.
[20]	李风亭. 我国混凝剂应用现状及问题探讨[J]. 净水技术, 2018,37(7):1-3,13.
[21]	李风亭, 任晓红. 雾化渍制备聚合硫酸铁新工艺[J]. 工业水处理, 1996,16(3):20-21.
[22]	李风亭, 陈辅君, 杜锡荣, 等. 混凝剂聚合硫酸铁反应机理的探讨[J]. 给水排水, 1994,31(8):39-40,5.
[23]	Li F, Ji G, Xue G. The preparation of inorganic coagulant-poly ferric sulfate[J]. Journal of Chemical Technology & Biotechnology 1997,68(2):219-221.
[24]	易佑华, 蒋新月, 易玲. 固体型聚合硫酸铁的生产方法:中国,1105342[P]. 1995-07-19.

类别	名称	对应标准
无机小分子	硫酸铝	GB/T 31060—2014
	氯化硫酸铁	无
	硫酸铁	参考GB 14591—2006
	硫酸铝铁	HG/T 5565—2019
	硫酸亚铁	GB/T 10531—2016
	氯化铁	GB/T 4482—2018
无机高分子聚氯化铝固体300万t/a液体聚硫酸铁和聚氯化铁600万t/a	聚氯化铝	GB 15892—2020饮用水用 GB/T 22627—2014工业水处理
	聚硫酸铝	HG/T 5006—2016
	聚氯化铁	HG/T 4672—2014
	聚硫酸铁	GB 14591—2006
	聚硫酸铁铝	参考GB 14591—2006
	聚硅氯化铝	参考GB/T 22627—2014
	聚硅硫酸铝	HG/T 4537—2013
	聚硅氯化铝铁	HG/T 5359—2018
	聚硅硫酸铁	参考GB 14591—2006
	聚硅硫酸铝铁	HG/T 4537—2013

牌号	w（Al₂O₃）	w（Na₂O）	w（Fe₂O₃）	w（SiO₂）	w（水分）	酸溶率
HY-01	≥64.5	≤0.50	≤0.02	≤0.02	≤20	≥96
HY-02	≥64.0	≤0.80	≤0.04	≤0.04	≤20	≥94

指标标准和产品		外观	密度（20 ℃）/ （g·cm^-3）	w（Al₂O₃）/ %	盐基度/ %	w（不溶物）/ %	浊度 NTU	pH（10 g/L 溶液）	w（Fe）/ 10^-6	w（Mn）/ 10^-6
欧盟EN883—2004		无色至黄色	1.16~1.40	7.9~17.9	>35	—	—	—	—	—
美国ANSI/AWWA B408—2010		无色至淡黄色	—	5.0~25.0	10~63	—	≤50	—	—	—
日本JIS/K1475—2006		无色至淡褐色	≥1.19	10~11	45~65	—	—	3.5~5.0	≤100	≤15
GB 15892—2020	液	无色至淡黄色	≥1.12	≥10.0	45.0~90.0	≤0.1	—	3.5~5.0	≤0.2	—
GB 15892—2020	固	白色至淡黄色	—	≥29.0	45.0~90.0	≤0.1	—	3.5~5.0	≤0.2	—
指标标准和产品		w（CN）/ 10^-6	w（Pb）/ 10^-6	w（Cd）/ 10^-6	w（Cr）/ 10^-6	w（Cr⁶⁺）/ 10^-6	w（Hg）/ 10^-6	w（As）/ 10^-6	w（SO₄^2-）/ %
欧盟EN883—2004		—	2.12~42.34	0.16~5.29	1.59~52.93	—	0.21~1.06	0.74~5.29	—
美国ANSI/AWWA B408—2010		—	—	—	—	—	—	—	—
日本JIS/K1475—2006		≤100	≤5	≤1	≤5	—	≤0.1	≤1	≤3.5
GB 15892—2020	液	—	≤5	≤1	≤5	—	≤0.1	≤1	—
GB 15892—2020	固	—	≤5	≤1	≤5	—	≤0.1	≤1	—

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会