Abstract: <SPAN lang=EN-US style="FONT-SIZE: 10.5pt; FONT-FAMILY: "Times New Roman"; mso-bidi-font-size: 12.0pt; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA; mso-fareast-font-family: 宋体">Aluminum hydroxide powders with different crystal morphologies were prepared by carbonation method from sodium metaaluminate solution under different technological conditions.Stability of red phosphorus coated by nano-sized aluminum hydroxide powders with different morphologies was studied.Ultrafine red phosphorus was encapsulated with nano-sized aluminum hydroxide powders by methods of sol-gel and precipitation,respectively.Prepared Al(OH)</SPAN><SPAN lang=EN-US style="FONT-SIZE: 10.5pt; FONT-FAMILY: "Times New Roman"; mso-bidi-font-size: 12.0pt; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA; mso-fareast-font-family: 宋体"><SUB>3</SUB> coated red phosphorus was characterized by means of DTA,water absorption rate test,SEM,and IR etc.,and various technological factors which had effects on the encapsulating result were also studied.Experiment results indicated that the stability of the micro-encapsulated red phosphorus prepared by sol-gel method with flaky nano-Al(OH)</SPAN><SPAN lang=EN-US style="FONT-SIZE: 10.5pt; FONT-FAMILY: "Times New Roman"; mso-bidi-font-size: 12.0pt; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA; mso-fareast-font-family: 宋体"><SUB>3</SUB> solution as coating agent was better,and which even had a higher ignition point than that encapsulated by organic colophony.</SPAN><SPAN style="FONT-SIZE: 10.5pt; FONT-FAMILY: 宋体; mso-bidi-font-size: 12.0pt; mso-ascii-font-family: "Times New Roman"; mso-hansi-font-family: "Times New Roman"; mso-bidi-font-family: "Times New Roman"; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA"></SPAN>