碳化硼微粉的低温合成

Abstract

Abstract: Polyvinyl borate gel was prepared with polyvinyl alcohol (PVA) and boron acid as raw materials,which was employed as precursor for preparing boron carbide and then it was pyrolyzed and reduced to form boron carbide powder by carbonthermal process.Effects of amount-of-substance ratio of polyvinyl alcohol to boron acid,pyrolyzed temperature of the precursor, carbonthermal reduction temperature,and reduction time of pyrolyzed precursor on boron carbide synthesis were respectively investigated.Intermediate and product were respectively characterized by FT-IR,chemical composition,XRD,SEM,and particle size analysis etc..Results indicated that the optimum raw material mix ratio for precursor polyvinyl borate was n(PVA)∶n(boron acid)=4∶1；B₄C powder with a primary particle size of 10 μm could be obtained when the precursor was pyrolyzed at 600 ℃ for 2 h,and then treated at 1 300 ℃ for 2 h.

Key words: boron carbide, polyvinyl alcohol, sol-gel method

CLC Number:

TQ128.1

ZHANG Yun-Fei, ZHONG Jian-Chu, WANG Hong-Zhi. Low temperature synthesis of boron carbide micropowder[J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(10): 29-.

[1]	Chen Guanting,Li Sanxi,Wang Song,Li Yang. Research progress of boron carbide powder prepared by precursor derived method [J]. Inorganic Chemicals Industry, 2020, 52(2): 6-11.
[2]	Zhao Hongkai,Peng Zhenfeng,Chi Mingshuo. Research status of silicon oxide nanowires [J]. Inorganic Chemicals Industry, 2020, 52(11): 12-15.
[3]	Yu Tianhua,Ao Houyu,Huang Qipeng,Wu Jinglan. Preparation and catalytic hydroxylation performance of hierarchical titanium silicalite-1 [J]. Inorganic Chemicals Industry, 2019, 51(9): 102-105.
[4]	Zhou Peng1，2，Guo Qiushuang1，2，Li Xiaoyun1，2，Sun Yanmin1，2，Miao Jing1，Yu Haibin1，2. Application of mesoporous TiO2-SiO2 composite oxide inphotocatalytic degradation of Rhodamine B [J]. Inorganic Chemicals Industry, 2019, 51(7): 93-99.
[5]	WANG Guo-Ming, MA Xue-Ming, WU Ping, YANG Sheng-Bin. Magnetic and photo-catalytic properties of Zn-Mn co-doped BiFeO3 nano-crystals [J]. INORGANICCHEMICALSINDUSTRY, 2016, 48(9): 83-.
[6]	LI De-Gui, ZHANG Jin-Lei, QIN Ming, DENG Yu-Ping. Preparation of La2O3 powder and effect on grain size [J]. INORGANICCHEMICALSINDUSTRY, 2014, 46(11): 21-.
[7]	ZHU Jian-Jun, JIANG De-Li, WEI Wei, XIE Ji-Min. Analysis on transmittance of hydrophobic silica aerogels prepared at ambient pressure [J]. INORGANICCHEMICALSINDUSTRY, 2013, 45(12): 21-.
[8]	YANG Bao-Ping, ZHONG Xiao-Hua, ZHANG Xiao-Liang, CUI Jin-Feng, JIA Jun-Hong, YI Ge-Wen. Effects of Sb doping amount on structure and transmission,electric property of ATO films [J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(1): 19-.
[9]	ZHANG Wang-Xi, YUAN Zu-Pei, WANG Yan-Zhi. Study on preparation process of yttria stabilized nano-sized zirconia [J]. INORGANICCHEMICALSINDUSTRY, 2012, 44(1): 22-.
[10]	WU Yuan-Ting, WANG Xiu-Feng, TONG Xiao-Fei. Synthesis of ultrafine silica powders by Pechini sol-gel method [J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(6): 17-.
[11]	HAO Pin, HUANG Jian-Feng, CAO Li-Yun, WU Jian-Peng, WANG Pei-Lin. Effect of pH on nickel titanate nanocrystallites synthesized by sol-gel method [J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(2): 17-.
[12]	WANG Peng-Cheng, LIU Song, LIU Meng-Xi. Study on preparation and dispersivity of monodisperse silica nanoparticles [J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(2): 40-.
[13]	Cai Aman;Ye Chaoxian;Li Hongqiang;Gao Qiongzhi;Zeng Xingrong;Lu Qingyuan. Preparation and characterization of nano-sized KH-570 modified [J]. INORGANICCHEMICALSINDUSTRY, 2010, 0(3): 0-0.
[14]	Yao Yan;Ma Liqun;Ding Yi;Wang Linying;Yang Meng. Study on improvement of electrochromic properties of tungstic oxide film by PVA-doping [J]. INORGANICCHEMICALSINDUSTRY, 2009, 0(8): 0-0.
[15]	Jia Zhigang;Li Yanhua. Research progress on synthesis of low-dimensional nano-structure for complex metal oxides [J]. INORGANICCHEMICALSINDUSTRY, 2009, 0(7): 0-0.

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Low temperature synthesis of boron carbide micropowder

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Metrics

Comments

Recommended 10