离子交换法合成硫酸钡的研究

doi:10.11962/1006-4990.2019-0475

摘要/Abstract

摘要：

碳酸钡与硫酸钾为原料,采用离子交换法合成硫酸钡,考察了工艺参数对硫酸钡产率的影响,并采用X射线衍射（XRD）、扫描电子显微镜（SEM）、傅里叶变换红外光谱（FTIR）等分析方法对产物晶相、形貌做了表征。结果表明：在c（SO₄ ^2-）=0.007 5 mol/L、液固质量比（g/g）为800∶1、反应温度为30 ℃、反应时间为72 h的最优条件下,硫酸钡的产率最高可达98.25%,得到的硫酸钡为规则的片状,结晶良好,纯度较高。

关键词: 离子交换法, 硫酸钡, 碳酸钡, 硫酸钾

Abstract:

Barium sulfate was synthesized by ion-exchange method,with barium carbonate and potassium sulfate as raw ma-terials.The effects of preparation parameters on the yield of barium sulfate was investigated.X-ray diffraction（XRD）,scan-ning electron microscopy（SEM） and Fourier transform infrared spectroscopy（FTIR） were used to characterize crystalline and morphology.The results showed that the yield of barium sulfate was up to 98.25% under the optimal conditions,such as c（SO₄ ^2-）=0.007 5 mol/L,liquid-solid mass ratio of 800∶1（g/g）,reaction temperature of 30 ℃ and reaction time of 72 h.The obtained barium sulfate was regular flake with crystalline integrity and high purity.

Key words: ion-exchange method, barium sulfate, barium carbonate, potassium sulfate

中图分类号:

TQ132.35

张鹏,张煜,段江飞,林小华. 离子交换法合成硫酸钡的研究[J]. 无机盐工业, 2020, 52(5): 40-44.

Zhang Peng,Zhang Yu,Duan Jiangfei,Lin Xiaohua. Research on synthesis of barium sulfate by ion-exchange method[J]. Inorganic Chemicals Industry, 2020, 52(5): 40-44.

图/表 13

图1

图2

图3

图4

图5

图6

表1

表2

表3

图7

表4

图8

图9

参考文献 15

[1]	祁琪, 孙青, 张俭 , 等. 超细沉淀硫酸钡的制备及研究进展[J]. 无机盐工业, 2018,50(5):15-20.
[2]	Ke Z, Bai Y P . Improve the gas barrier property of PET film with montmorillonite by in situ interla-yer polymerization[J]. Materials Letters, 2005,59(27):3348-3351.
[3]	曹荣 . 功能性微细硫酸钡的制备研究[D]. 天津:河北工业大学, 2012.
[4]	Meagher M J, Leone B, Turnbull T L . Dextran-encapsulated barium sulfate nanoparticles prepared for aqueous dispersion as an X-ray contrast agent[J]. J.Nanopart Res., 2013,15:2146.Doi: 10.1007/s11051-013-2146-8.
[5]	尚方毓, 胡昉, 苏小红 . 浅谈国内沉淀硫酸钡生产现状及发展趋势[J]. 无机盐工业, 2015,47(1):1-4.
[6]	阎振宗, 董晓菁, 段亚宏 . 碳酸钡芒硝转化法生产硫酸钡[J]. 河北化工, 2013,36(3):56-57.
[7]	尚久芳, 操时杰, 辛无名 , 等. 兰式化学手册[D]. 北京: 科学出版社, 1991.
[8]	Zhao Chenhao, Liu Fenglin, Kang Wenpei , et al. An ion-exchange approach to the crystal design of barium sulfate in the presence of ionic surfactants[J]. Cryst.Growth Des., 2011,11:2084-2090.
[9]	祁琪, 孙青, 张俭 , 等. EDTA络合-球磨法制备超细棒状BaSO₄[J]. 高校化学工程学报, 2019,33(3):732-737.
[10]	Haley L V, Mattioli T A, Wiles DR . Micro-Raman study of sulphate coprecipitated with potassium ions[J]. Journal of Raman Spectro-scopy, 1987(18):101-104.
[11]	樊先平, 洪樟连, 翁文剑 . 无机非金属材料科学基础[M]. 杭州: 浙江大学出版社, 2004.
[12]	Liu Yuejiao, Guo Xiaoyao, Yang Suohe , et al. Controllable preparation of uniform micronsized barium sulfate spheres[J]. Crystal Research & Technology, 2018,53(6).Doi: 10.1002/crat.201700212.
[13]	李丽匣, 韩跃新, 陶世杰 . 碳酸钙晶须表面改性研究[J]. 化工矿物与加工, 2008,37(5):4-8.
[14]	闻辂, 梁婉雪, 章正刚 . 矿物红外光谱学[M]. 重庆: 重庆大学出版社, 1988.
[15]	张明, 李新海, 胡启阳 , 等. EDTA络合法合成硫酸钡微粒[J]. 中国有色金属学报, 2009,19(8):1512-1516.

序号	因素
序号	A 反应温度/℃	B 液固比/（g·g^-1）	C c（SO₄^2-）/（mol·L^-1）
1	20	600∶1	0.005
2	30	800∶1	0.075
3	40	1 000∶1	0.010

序号	因素			转化率/%
序号	A	B	C	转化率/%
1	1	1	1	79.21
2	1	2	2	96.82
3	1	3	3	97.01
4	2	1	2	90.26
5	2	2	3	98.25
6	2	3	1	84.89
7	3	1	3	88.26
8	3	2	1	81.54
9	3	3	2	96.22
K₁	273.04	257.73	245.64
K₂	273.40	276.61	283.30
K₃	266.02	278.12	283.52
R	7.38	20.39	37.88

因素	偏差平方和	自由度	F值	显著度
A	11.542	2	3.61
B	86.054	2	26.89	*
C	317.024	2	99.07	**
误差	3.19	2

晶面	2θ/（°）	结晶度/%	晶面	2θ/（°）	结晶度/%
（111）	22.71	94.95	（211）	31.45	92.83
（021）	25.81	90.99	（140）	42.59	93.72
（210）	26.80	92.13	（212）	42.88	88.41
（121）	28.72	89.37