固液反萃湿法磷酸生产磷铵的工艺研究

摘要/Abstract

摘要： 通过连续逆流萃取对原料湿法磷酸先进行净化，萃取后的有机溶剂相直接用氨反萃取生成磷铵晶体，再沉降使晶体与有机萃取剂分离，实现磷铵直接反萃结晶和萃取剂的循环利用。结果表明用氨直接固液反萃湿法磷酸生产磷铵的最佳工艺条件是：萃取剂组成为V(磷酸三丁酯)∶V(稀释剂)=1∶1，原料磷酸浓度为w（P₂O₅）=40%～50%，萃取剂用量为V(萃取剂)∶V(原料磷酸)≈3∶1，萃取搅拌时间约为5 min，氨用量控制为氨反萃结晶后的液相pH≈7，固液反萃-结晶温度为15～20 ℃。最终所得的磷铵晶体中w(氮)＞20%、w(五氧化二磷)＞50%，原料湿法磷酸中的五氧化二磷一次性利用率接近50%。该法所得磷铵晶体中氮磷含量均接近工业磷酸二铵(98%)标准，远大于国家肥料级农用磷铵产品标准。

关键词: font-family: 宋体, mso-bidi-font-size: 12.0pt, mso-ascii-font-family: 'Times New Roman', mso-hansi-font-family: 'Times New Roman', mso-bidi-font-family: 'Times New Roman', mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, 湿法磷酸')">mso-bidi-language: AR-SA">湿法磷酸, 磷铵, 固液反萃

Abstract: Method of continuous countercurrent extraction was used to purify raw material phosphoric acid by wet process at first.Then ammonia was used to directly back extract the organic solvent after extraction to produce ammonium phosphate crystals.Finally the crystals were separated from the organic extraction agent by deposition to achieve the aim of recycling utilization of organic extraction agent and direct crystallization of ammonium phosphate through back extraction.Experiment results showed that the optimum technological conditions of producing ammonium phosphate with the method of solid-liquid back extraction of wet process phosphoric acid were as follows：extractants′ composition was V(tributyl phosphate)∶V(diluent)=1∶1，mass fraction of P₂O₅ in raw material phosphoric acid was at 40%~50%，volume ratio of extractants to phosphoric acid was about 3∶1，extraction stirring time was about 5 min，ammonia amount was that control pH≈7 of the liquid phase after backextracted crystallization,and stripping-crystallization temperature was 15~20 ℃.Ultimately in the obtained ammonium phosphate crystalsw(N)>20%andw(P₂O₅)>50%，and one time utilization ratio of P₂O₅in the phosphoric acid by wet process approached 50%.Contents of N and P in ammonium phosphate crystals made by this method were both close to the industrial DAP (98%) standard and were much higher than national fertilizer grade ammonium phosphate product standard.

Key words: font-family: "Times New Roman", mso-bidi-font-size: 12.0pt, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, phosphoric acid by wet processmso-fareast-font-family: 宋体">phosphoric acid by wet processfont-family: 宋体, mso-bidi-font-size: 12.0pt, mso-ascii-font-family: 'Times New Roman', mso-hansi-font-family: 'Times New Roman', mso-bidi-font-family: 'Times New Roman', mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, ；mso-bidi-language: AR-SA">；font-family: "Times New Roman", mso-bidi-font-size: 12.0pt, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, ammonium phosphatemso-fareast-font-family: 宋体">ammonium phosphatefont-family: 宋体, mso-bidi-font-size: 12.0pt, mso-ascii-font-family: 'Times New Roman', mso-hansi-font-family: 'Times New Roman', mso-bidi-font-family: 'Times New Roman', mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, ；mso-bidi-language: AR-SA">；font-family: "Times New Roman", mso-bidi-font-size: 12.0pt, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, solid-liquid back extraction ')">mso-fareast-font-family: 宋体">solid-liquid back extraction

熊祥祖, 张林锋, 魏世辕, 李志保, 李文歆. 固液反萃湿法磷酸生产磷铵的工艺研究[J]. 无机盐工业, 2011, 43(1): 36-39.

XIONG Xiang-Zu, ZHANG Lin-Feng, WEI Shi-Yuan, LI Zhi-Bao, LI Wen-Xin. Research on process of producing ammonium phosphate with solid-liquid back extraction of phosphoric acid by wet process[J]. INORGANICCHEMICALSINDUSTRY, 2011, 43(1): 36-39.

[1]	杨韩,邓伏礼,丁瑶,龙秉文. 枸溶性磷淤渣综合利用实验研究[J]. 无机盐工业, 2022, 54(12): 87-91.
[2]	陶俊法1, 杨建中2. 中国磷化工行业现状和发展方向[J]. 无机盐工业, 2011, 43(1): 1-3.
[3]	梅毅1, 樊蕾2, 梁雪松2, 赵建国2. 热法磷酸与湿法工业磷酸的技术经济分析[J]. 无机盐工业, 2011, 43(1): 4-7.
[4]	马力言, 陈为亮, 李楠, 王迎爽, 张殿彬. 硅钢级氧化镁的研究进展[J]. 无机盐工业, 2011, 43(1): 8-11.
[5]	孙亚光, 赵留喜, 余丽秀. 中国主要化工副产硅资源利用技术进展及评述[J]. 无机盐工业, 2011, 43(1): 12-14.
[6]	罗炳威1, 3, 邓天龙1, 2, 李丹1. 三元体系Mg₂+//Cl^-, borate —H₂O在323.15 K时相平衡研究[J]. 无机盐工业, 2011, 43(1): 15-18.
[7]	贺小昆, 刘沁曦, 覃庆高, 郭律. 镧钡改性氧化铝负载钯、铑的催化活性研究[J]. 无机盐工业, 2011, 43(1): 19-21.
[8]	谈廷风1, 2, 卞曙光3, 齐鹏1, 王世荣1, 安永1, 李祥高1. 中空黑色一氧化钛粒子的制备、改性及电泳性能[J]. 无机盐工业, 2011, 43(1): 22-24.
[9]	傅小明, 刘照文, 薛珊珊. 二水草酸镍在空气中热分解过程的研究[J]. 无机盐工业, 2011, 43(1): 25-26.
[10]	门智新, 孙奉娄, 何翔. 沉淀法制备羟基磷灰石反应条件控制研究[J]. 无机盐工业, 2011, 43(1): 27-29.
[11]	李志林1, 安青珍1, 郝永亮2. 凹凸棒土负载氧化锌-二氧化钛的制备与性能[J]. 无机盐工业, 2011, 43(1): 33-35.
[12]	杨荣华 , 高德力. 用天然石膏制备硫酸铵和氯化钙的工艺研究[J]. 无机盐工业, 2011, 43(1): 40-42.
[13]	程忠俭, 郭娜, 张娟. 高纯硝酸锶的工艺研究[J]. 无机盐工业, 2011, 43(1): 43-44.
[14]	张义勇, 师敏, 于雪峰, 胡成银. 石灰石-苦卤法、氨法制备高纯镁砂工艺比较[J]. 无机盐工业, 2011, 43(1): 45-47.

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会