硼酸喷雾包覆改性镍钴铝酸锂的制备及其电化学性能研究

doi:10.19964/j.issn.1006-4990.2021-0190

摘要/Abstract

摘要：

针对镍钴铝酸锂（NCA）三元正极材料普遍存在的循环寿命差、浆料容易凝胶等缺点进行了硼酸喷雾包覆的改性。采用X 射线衍射仪（XRD）、扫描电镜（SEM）、透射电镜（TEM）及电化学测试等方法对硼酸包覆改性前后的材料性能进行了对比表征和分析。结果表明：喷雾包覆后可以在NCA正极材料表面形成一层保护层,改性后的NCA三元正极材料循环寿命有明显提升,特别是高温（45 ℃）1C/1C倍率下循环50次容量保持率由改性前的88.0%提升至改性后的95.2%,提升近7%;硼酸包覆可以改善NCA表面特性,使正极浆料稳定性大大提高。改性后的NCA正极浆料可以稳定放置168 h（7 d）,解决了NCA正极材料容易凝胶的问题。

关键词: 镍钴铝酸锂, 喷雾包覆, 硼酸

Abstract:

Boric acid spray coating was used to modify lithium nickel-cobalt aluminate（NCA） ternary cathode materials for their poor cycle life and poor slurry stability.The properties of boric acid coated materials were characterized and analyzed by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM） and electrochemical tests.The results showed that a protective layer could be formed on the surface of NCA cathode material after spray coating,and the cycle life of NCA ternary-element cathode material after modification was significantly improved,especially the capa-city retention rate of 1C/1C 50 cycles at high temperature（45 ℃） was increased from 88.0% to 95.2% after modification,in-creasing by nearly 7 percentage points.Boric acid coating could improve the surface characteristics of NCA and greatly impro-ved the stability of positive electrode paste.The modified NCA positive electrode paste could be stably placed for 168 h （7 d）,which solved the problem that NCA positive electrode material was easy to gel.

Key words: lithium nickel-cobalt aluminate, spray coating, boric acid

中图分类号:

TQ131.11

邹昌武,孙玖,范未峰,张彬,王政强,张郑. 硼酸喷雾包覆改性镍钴铝酸锂的制备及其电化学性能研究[J]. 无机盐工业, 2022, 54(1): 66-70.

ZOU Changwu,SUN Jiu,FAN Weifeng,ZHANG Bin,WANG Zhengqiang,ZHANG Zheng. Study on preparation and electrochemical properties of lithium nickel cobalt aluminate modified by boric acid spray coating[J]. Inorganic Chemicals Industry, 2022, 54(1): 66-70.

图/表 8

图1

图2

图3

图4

图5

图6

图7

图8

参考文献 17

[1]	谢元, 李俊华, 王佳, 等. 锂离子电池三元正极材料的研究进展[J]. 无机盐工业, 2018, 50(7):18-22.
[2]	熊凡, 王同振, 高强, 等. Li₂MnO₃复合LiNi_0.8Co_0.1Mn_0.1O₂材料制备及电化学性能研究[J]. 无机盐工业, 2020, 52(1):68-72.
[3]	YOON C S, KIM U H, PARK G T, et al. Self-passivation of a LiNiO₂ cathode for a lithium-ion battery through Zr doping[J]. ACS Energy Letters, 2018, 3(7):1634-1639. doi: 10.1021/acsenergylett.8b00805
[4]	KONDO H, TAKEUCHI Y, SASAKI T, et al. Effects of Mg-substitu-tion in Li(Ni,Co,Al)O₂ positive electrode materials on the crys-tal structure and battery performance[J]. Journal of Power Sources, 2007, 174(2):1131-1136. doi: 10.1016/j.jpowsour.2007.06.035
[5]	KONG D F, HU J T, CHEN Z F. Ti-gradient doping to stabilize lay-ered surface structure for high performance high-Ni oxide cathode of Li-ion battery[J]. Advanced Energy Materials, 2019, 9(41).Doi: 10.1002/aenm.201901756. doi: 10.1002/aenm.201901756
[6]	PARK K J, JUNG H G, KUO L Y, et al. Improved cycling stability of Li[Ni_0.90Co_0.05Mn_0.05]O₂ through microstructure modification by boron doping for Li-ion batteries[J]. Advanced Energy Materials, 2018, 8(25).Doi: 10.1002/aenm.201801202. doi: 10.1002/aenm.201801202
[7]	郭孝东, 徐春柳, 向伟, 等. 富镍三元正极材料的改性研究进展[J]. 工程科学与技术, 2020, 52(1):9-15.
[8]	NEUDECK S, STRAUSS F, GARCIA G. Room temperature,liquid-phase Al₂O₃ surface coating approach for Ni-rich layered oxide ca-thode material[J]. Chemical Communications, 2019, 55(15):2174-2177. doi: 10.1039/C8CC09618J
[9]	SONG B, LI W, OH S M, et al. Long-life nickel-rich layered oxide cathodes with a uniform Li₂ZrO₃ surface coating for lithium-ion bat-teries[J]. ACS Appl Mater Interfaces, 2019, 9(11):9718-9725. doi: 10.1021/acsami.7b00070
[10]	WU G, ZHOU Y K. TiP₂O₇-coated LiNi_0.8Co_0.15Al_0.05O₂ cathode ma-terials with improved thermal stability and superior cycle life[J]. Journal of Energy Chemistry, 2019, 28:151-159. doi: 10.1016/j.jechem.2018.01.018
[11]	XIE Z C, ZHANG Y Y, YUAN A B, et al. Effects of lithium excess and SnO₂ surface coating on the electrochemical performance of LiNi_0.8Co_0.15Al_0.05O₂ cathode material for Li-ion batteries[J]. Journal of Alloys and Compounds, 2019, 787:429-439. doi: 10.1016/j.jallcom.2019.02.127
[12]	SUBRAMANIAN V, FEY G T K. Preparation and characterization of LiNi_0.7Co_0.2Ti_0.05M_0.05O₂(M=Mg,Al and Zn) systems as cathode ma-terials for lithium batteries[J]. Solid State Ionics, 2002, 148(3):351-358. doi: 10.1016/S0167-2738(02)00073-5
[13]	LIU Z, WANG Z, LU T, et al. Modification of LiNi_0.8Co_0.15Al_0.05O₂ using nanoscale carbon coating construction[J]. Journal of Alloys & Compounds, 2018, 763:701-710.
[14]	郭宇, 黄玲, 肖方明, 等. 高镍系Li[(Ni_0.88Co_0.12)_0.9(Ni_0.8Co_0.15Al_0.05)_0.1]O₂正极材料的制备研究[J]. 电源技术, 2020, 40(1):13-16.
[15]	陈俊辉, 陈均青, 卑凤利, 等. 石墨烯包覆钴铝酸锂的制备及其在高电压下电化学性能的研究[J]. 化工新型材料, 2020, 48(6):118-121.
[16]	QI R, SHI J, ZHANG X, et al. Improving the stability of LiNi_0.8Co_0.15Al_0.05O₂ by AlPO₄ nanocoating for lithium-ion batteries[J]. Science China Chemistry, 2017, 60(9):1230-1235. doi: 10.1007/s11426-017-9050-6
[17]	YANG C, SHAO R, MI Y, et al. Stable interstitial layer to alleviate fatigue fracture of high nickel cathode for lithium-ion batteries[J]. Journal of Power Sources, 2018, 376:200-206. doi: 10.1016/j.jpowsour.2017.11.085

首页

全国无机盐信息中心

中国化工学会

无机酸碱盐专业委员会