Cause analysis of early cycling attenuation of LiFePO4 battery and its performance improvement
Received date: 2022-06-20
Online published: 2023-03-17
LiFePO4 battery is highly favored for its′excellent cycling performance，relatively low price and high stability.The cyclic curve faded rapidly in the early stage，and flattened out in the middle and late stages.In order to explore the potential capacity of LiFePO4 battery for longer service life，LiFePO4/graphite battery was taken as the research object to study the early cycle with fast decay，and suggestions for improvement were put forward based on the research results.Compared with the ternary（NCM） cell，the differences of initial efficiency of the anode material caused the cycle attenuation of LiFePO4 material to be faster than that of the ternary material.This theory had been confirmed by means of inductively coupled plasma emission spectroscopy（ICP），X-ray diffraction（XRD），etc.The SEI films were characterized by inductively coupled plasma emission spectroscopy（ICP），energy dispersive spectroscopy（EDS） and differential scanning calorimetry（DSC）.It was proved that the main reason for the fast decay of LiFePO4 in the early stage was the consumption of active lithium，and the loss of active lithium was mainly used to repair the damaged SEI film.Finally，the decay rate of the LiFePO4 battery in the early stage could be slowed down by improving the OI value of the negative particles，the coating amount of the cathodes，the swelling of the negative gel，and the specific surface area of the anodes.
XU Ruilin , ZENG Tao , LIU Huan , LIU Xingwei , WANG Hao , XU Xiaoming , ZHAO Lipeng . Cause analysis of early cycling attenuation of LiFePO4 battery and its performance improvement[J]. Inorganic Chemicals Industry, 2023 , 55(3) : 92 -97 . DOI: 10.19964/j.issn.1006-4990.2022-0275
| 1 | 张克杰，陈鹏，谢旺旺，等.磷酸铁锂优缺点及改性研究进展[J].无机盐工业，2018，50（6）:13-17. |
| ZHANG Kejie， CHEN Peng， XIE Wangwang，et al.Progress in modification of lithium iron phosphate and its advantages and disadvantages[J].Inorganic Chemicals Industry，2018，50（6）:13-17. | |
| 2 | 曹利娜，王晨旭，刘成士，等.磷酸铁锂正极材料与电解液的相容性研究[J].无机盐工业，2014，46（10）:75-78. |
| CAO Lina， WANG Chenxu， LIU Chengshi，et al.Study on compatibility of LiFePO4 cathode material with electrolyte for lithium ion battery[J].Inorganic Chemicals Industry，2014，46（10）:75-78. | |
| 3 | HUANG Xiankun， HE Xiangming， JIANG Changyin，et al.Reaction mechanisms on solvothermal synthesis of nano LiFePO4 crystals and defect analysis[J].Industrial & Engineering Chemistry Research，2017，56（38）:10648-10657. |
| 4 | 黄可龙，吕正中，刘素琴.锂离子电池容量损失原因分析[J].电池，2001，31（3）:142-145. |
| HUANG Kelong， LU Zhengzhong， LIU Suqin.On capacity fading and its mechanisms for lithium-ion batteries[J].Battery Bimonthly，2001，31（3）:142-145. | |
| 5 | 王其钰，王朔，张杰男，等.锂离子电池失效分析概述[J].储能科学与技术，2017，6（5）:1008-1025. |
| WANG Qiyu， WANG Shuo， ZHANG Jienan，et al.Overview of the failure analysis of lithium ion batteries[J].Energy Storage Science and Technology，2017，6（5）:1008-1025. | |
| 6 | 李昭宇，李红朝，陶亮，等.LiFePO4/石墨电池高温循环失效分析[J].电池，2022，52（4）:396-400. |
| LI Zhaoyu， LI Hongchao， TAO Liang，et al.Cycle failure analysis of LiFePO4/graphite battery at high temperature[J].Battery Bimonthly，2022，52（4）:396-400. | |
| 7 | 刘晓梅，姚斌，谢乐琼，等.磷酸铁锂动力电池常温循环衰减机理分析[J].储能科学与技术，2021，10（4）:1338-1343. |
| LIU Xiaomei， YAO Bin， XIE Leqiong，et al.Analysis of the capacity fading mechanism in lithium iron phosphate power batteries cycled at ambient temperatures[J].Energy Storage Science and Technology，2021，10（4）:1338-1343. | |
| 8 | 吴小兰，王光俊，陈炜，等.复合三元电池高温循环劣化分析[J].电池，2017，47（6）:347-350. |
| WU Xiaolan， WANG Guangjun， CHEN Wei，et al.Degradation analysis of composite ternary battery after high temperature cycle[J].Battery Bimonthly，2017，47（6）:347-350. | |
| 9 | 阮一钊，田艳红，李守涛，等.LiNi0.5Co0.2Mn0.3O2/石墨电池高温失效的机理[J].电池，2020，50（3）:220-223. |
| RUAN Yizhao， TIAN Yanhong， LI Shoutao，et al.High temperature failure mechanism of LiNi0.5Co0.2Mn0.3O2/graphite battery[J].Battery Bimonthly，2020，50（3）:220-223. | |
| 10 | YANG Yue.Capacity fade characteristics of lithium iron phosphate cell during dynamic cycle[J].Energy，2020，206.Doi:10.1016/j.energy.2020.118155. |
| 11 | 倪江锋，周恒辉，陈继涛，等.锂离子电池中固体电解质界面膜（SEI）研究进展[J].化学进展，2004，16（3）:335-342. |
| NI Jiangfeng， ZHOU Henghui， CHEN Jitao，et al.Progress in solid electrolyte interface in lithium ion batteries[J].Progress in Chemistry，2004，16（3）:335-342. | |
| 12 | 王利.磷酸铁锂电极界面反应机制研究[D].徐州:中国矿业大学，2016. |
| WANG Li.Electrode/electrolyte interfaces reaction mechanisms studies of LiFePO4[D].Xuzhou:China University of Mining and Technology，2016. | |
| 13 | 王振，李建玲，王康康，等.磷酸铁锂/石墨动力电池衰退机理分析[J].稀有金属与硬质合金，2020，48（3）:60-66. |
| WANG Zhen， LI Jianling， WANG Kangkang，et al.Analysis of capacity fading mechanisms of LiFePO4/graphite power battery[J].Rare Metals and Cemented Carbides，2020，48（3）:60-66. | |
| 14 | MING Jun， CAO Zhen， WU Yingqiang，et al.New insight on the role of electrolyte additives in rechargeable lithium ion batteries[J].ACS Energy Letters，2019，4（11）:2613-2622. |
| 15 | ZHANG Ningxin， TANG Huaqiong.Dissecting anode swelling in commercial lithium-ion batteries[J].Journal of Power Sources，2012，218:52-55. |
/
| 〈 |
|
〉 |