磷石膏填充墙研究现状与应用进展

doi:10.11962/1006-4990.2020-0272

Abstract

Abstract:

At present, the accumulated amount of waste phosphogypsum in China has reached 3×10 ⁸ tons, which causes waste of land resources and environmental damage.Using phosphogypsum in infilled wall system can not only achieve solid waste utilization, but also save energy, which is advantageous to economic development.During the “two sessions” in 2020, deputies to the National People's Congress proposed to comprehensively implement the “production based slag” policy.In order to speed up the ecological green and high-quality development process of phosphorus chemical industry in China, based on the research and development status of phosphogypsum at home and abroad, the advantages and disadvantages of phosphogypsum were summarized and the development potential of phosphogypsum infilled walls were explored.Combined with the actual application status of phosphogypsum infilled walls, the shortcomings of phosphogypsum used in infilled walls structure system were found.Finally, the research and application direction of phosphogypsum infilled walls were prospected, which could provide reference for assembly type phosphogypsum infilled walls and help the sustainable development of phosphorus chemical industry.

Key words: utilization of solid waste, production based slag, phosphogypsum infilled walls, assembly type

CLC Number:

TQ177.375

Yuan Shucheng,Liu Xiangling,Liang Wei,Zou Zuyin. Research status and application progress of phosphogypsum infilled walls[J]. Inorganic Chemicals Industry, 2021, 53(4): 8-13.

Figures/Tables 8

Fig.1

Table 1

Fig.2

Table 2

Fig.3

Fig.4

Fig.5

Fig.6

References 58

[1]	Koch W J, Douglas K S, Nicholls T L , et al. Current status and future trends[M]∥ Psychological Injuries. Oxford University Press, 2005.
[2]	廖莹 . 论磷石膏的综合利用现状及发展方向[J]. 化工设计, 2018,28(4):27-29, 1.
[3]	陈家伟 . 磷石膏综合利用处置方案[J]. 广州化工, 2019,47(1):109-111, 120.
[4]	叶学东 . 2017 年我国磷石膏利用现状、形势分析及措施[J]. 硫酸工业, 2018(8):1-4.
[5]	王逸 . 磷石膏农业资源化的利用技术与应用研究[D]. 广州:华南理工大学, 2016.
[6]	张逸超 . 新型现浇磷石膏填充墙力学性能与保温技术研究[D]. 武汉:武汉理工大学, 2017.
[7]	Rashad A M . Phosphogypsum as a construction material[J]. Journal of Cleaner Production, 2017,166(10):732-743.
[8]	佚名 . “十三五”节能减排综合工作方案[J]. 中国建材, 2017,15(3):10.
[9]	佚名 . 贵州磷石膏将执行“以用定产”、“消大于产”的政策[J]. 硫酸工业, 2018(6):8.
[10]	佚名 . 关于进一步做好禁止使用实心粘土砖工作的意见[J]. 节能与环保, 2004(3):3-4.
[11]	杨三可, 刘代俊, 胡厚美 , 等. 用磷石膏生产建筑材料的新进展[J]. 硫磷设计与粉体工程, 2004(1):5-7, 49.
[12]	姚兵 . 建筑节能学研究[M]. 北京: 北京交通大学出版社, 2014.
[13]	刘婧 . 建筑节能[M]. 长沙: 中南大学出版社, 2014.
[14]	叶学东 . 2018年我国磷石膏利用现状、问题及建议[J]. 磷肥与复肥, 2019,34(7):1-4.
[15]	刘芳, 吴建华, 王冲 . 黄磷炉渣-磷石膏复合胶凝材料性能研究[J]. 材料导报, 2007,21(5A):530-532.
[16]	王其明 . 现浇石膏外墙钢筋砼高层网格盒式筒中筒结构研究与应用[D]. 天津:天津大学, 2012.
[17]	马林转, 宁平, 杨月红 , 等. 磷石膏预处理工艺综述[J]. 磷肥与复肥, 2007(3):62-63.
[18]	纪罗军, 陈强 . 我国磷石膏资源化利用现状及发展前景综述[J]. 硫磷设计与粉体工程, 2006(5):5-10, 53.
[19]	王莹, 王鹏起, 谭丹君 , 等. 磷石膏的预处理及在建材中的应用[J]. 建设科技, 2016(16):164-166.
[20]	谢超凌, 高惠民, 朱芳 . 磷石膏预处理及利用[J]. 云南化工, 2006(2):64-67.
[21]	朱志伟, 何东升, 陈飞 , 等. 磷石膏预处理与综合利用研究进展[J]. 矿产保护与利用, 2019,39(4):19-25.
[22]	李鉴明, 王国鑫, 周孝义 . 磷石膏预处理的工艺选择与关键设备选型[J]. 磷肥与复肥, 2019,34(7):23-25.
[23]	胡宏, 何兵兵, 薛绍秀 . α-半水石膏的制备与应用研究进展[J]. 新型建筑材料, 2015,42(4):44-48.
[24]	田键, 苑跃辉, 黄志林 , 等. 磷石膏的综合利用现状及建议[J]. 建材世界, 2018,39(4):38-40.
[25]	黄丹, 杨林, 曹建新 . 石膏砌块耐水性研究进展[J]. 广东化工, 2009,36(7):82-83, 116.
[26]	朱大勇, 王君, 金旭 , 等. 耐水型磷石膏砌块的制备及其防水机理的研究[J]. 新型建筑材料, 2017,44(1):68-70.
[27]	王锋, 冉林浦, 鞠传英 , 等. 磷石膏砌块耐水性研究[J]. 材料科学, 2019,5(9):518-524.
[28]	陈怀军, 石宗利 . 灰色关联分析在石膏基墙材实验研究中的应用[J]. 墙材革新与建筑节能, 2006(7):32-34, 3.
[29]	梁凡凡, 张华刚, 罗玚 , 等. 现浇磷石膏弹性模量和泊松比的初步试验研究[J]. 贵州大学学报:自然科学版, 2013,30(2):81-85.
[30]	Li Y B, Dai S B, Zhang Y C , et al. Preparation and thermal insulation performance of cast-in-situ phosphogypsum wall[J]. Journal of Applied Biomaterials and Fundamental Materials, 2018,16(s1):81-92.
[31]	卢亚琴, 张华刚, 罗玚 , 等. 现浇磷石膏墙体研究及性能试验分析[J]. 工业建筑, 2014,44(4):60-64, 103.
[32]	张华刚, 吴琴, 贾晓飞 , 等. 现浇磷石膏抗压强度的试验研究[J]. 湖南大学学报:自然科学版, 2016(3):127-134.
[33]	赵建华, 杨玉发, 王伟 . 磷石膏制耐水型石膏砌块的研究与应用[J]. 硫磷设计与粉体工程, 2008(1):15-18, 1.
[34]	Kumar S . Fly ash-lime-phosphogypsum hollow blocks for walls and partitions[J]. Building and Environment, 2003,38(2):291-295.
[35]	Ajam L, Ouezdou M B, Felfoul H S , et al. Characterization of the tunisian phosphogypsum and its valorization in clay bricks[J]. Construction & Building Materials, 2009,23(10):3240-3247.
[36]	Degirmenci N . Utilization of phosphogypsum as raw and calcined material in manufacturing of building products[J]. Construction & Building Materials, 2008,22(8):1857-1862.
[37]	吴琴, 张华刚, 贾晓飞 , 等. 现浇磷石膏应力-应变曲线试验研究[J]. 建筑结构学报, 2015,36(5):150-157.
[38]	李美, 彭家惠, 张建新 , 等. 磷建筑石膏的特性及其改性[J]. 硅酸盐通报, 2012,31(3):553-558.
[39]	罗玚, 张华刚, 梁凡凡 , 等. 现浇磷石膏抗压强度影响因素的试验研究[J]. 贵州大学学报:自然科学版, 2013,30(2):86-89.
[40]	李美 . 磷石膏品质的影响因素及其建材资源化研究[D]. 重庆:重庆大学, 2012.
[41]	海晓凤 . 新型耐水石膏基墙体材料制备及性能研究[J]. 当代化工, 2017,46(8):1604-1606, 1610.
[42]	张付奇, 李刚, 李洁 , 等. EPS轻质耐水石膏墙体材料制备与试验研究[J]. 材料导报, 2016,30(s1):424-427, 431.
[43]	贾晓飞, 秦冬冬 . 现浇磷石膏墙体均匀局部受压试验研究[J]. 科技创新与应用, 2015(7):15-16.
[44]	张华刚, 梁凡凡, 罗玚 , 等. 基于现浇磷石膏的节能与结构一体化新型墙体结构及其应用[J]. 贵州大学学报:自然科学版, 2013,30(1):104-110.
[45]	梁凡凡 . 现浇磷石膏-混凝土网格式框架组合墙轴心受压力学性能的理论分析和实验研究[D]. 贵州:贵州大学, 2013.
[46]	秦冬冬, 张华刚, 贾晓飞 , 等. 网格式框架的静力弹塑性分析[J]. 贵州大学学报:自然科学版, 2015,32(1):98-102.
[47]	卢亚琴, 马克俭, 张华刚 , 等. 高层磷石膏墙体网格式框架结构受力性能分析[J]. 工业建筑, 2012,42(4):56-59.
[48]	卢亚琴, 马克俭, 张华刚 , 等. 高层磷石膏墙体网格式框架结构在水平荷载作用下的简化计算[J]. 工业建筑, 2012,42(5):98-101, 105.
[49]	卢亚琴, 马克俭, 张华刚 , 等. 磷石膏墙体钢筋混凝土网格式框架结构动力反应数值分析[J]. 建筑结构学报, 2009,30(s2):36-40.
[50]	蔡越, 张逸超, 谢建业 . 现浇磷石膏填充墙RC框架结构抗震性能[J]. 文摘版:工程技术, 2016(4):32.
[51]	张逸超 . 新型现浇磷石膏填充墙力学性能与保温技术研究[D]. 武汉:武汉理工大学, 2017.
[52]	王虹航 . 节能、环保新型墙材澳大利亚速成墙首次引进我国[J]. 建材工业信息, 2003(3):45.
[53]	马克俭, 高国富, 张华刚 , 等. 空间网格式框架结构在多、高层大开间灵活划分房间石膏节能建筑中的研究与应用综述[J]. 空间结构, 2009,15(3):66-84.
[54]	马克俭, 高国富, 张华刚 , 等. 节能与结构一体化新型钢筋混凝土结构体系[J]. 贵州工业大学学报:自然科学版, 2008,37(4):33-43.
[55]	JC/T 829—2010 石膏空心条板[S].
[56]	JGJ/T 201—2010 石膏砌块砌体技术规程[S].
[57]	DBJ52T093—2019 磷石膏建筑材料应用统一技术规范[S].
[58]	汪家铭 . 磷石膏综合利用技术现状与前景展望[J]. 中国石油和化工经济分析, 2012(9):52-55.

w （可溶性磷）/%	绝热干强度/MPa	饱和湿强度/MPa	软化系数
0.00	4.6	2.5	0.55
0.20	4.3	3.4	0.79
0.40	3.4	3.1	0.93
0.60	3.7	3.0	0.83
0.80	3.2	2.9	0.90

检验项目		外观质量	尺寸偏差			表观密度/ （kg·m^-3）	平整度/ mm	断裂荷载/ kN	软化系数
检验项目		外观质量	长度/mm	高度/mm	厚度/mm	表观密度/ （kg·m^-3）	平整度/ mm	断裂荷载/ kN	软化系数
JC/T 698—2010合格品		第 6.1条	±3.0	±2.0	±1.0	实心≤1 000	≤1.0	≥1.5	≥0.60
检测结果	试件1	符合要求	-3.0	-2.0	0	871	0.5	4.852	0.71
	试件2	符合要求	-2.0	-2.0	0	877	0.6	4.925	0.76
	试件3	符合要求	-2.0	-2.0	0	863	0.6	4.751	0.70

National Inorganic Salts Information Center

Inorganic Acid-Base-Salt Committee of CIESC

Research status and application progress of phosphogypsum infilled walls

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 58

Related Articles 0

Metrics

Comments

Recommended 10