利用多种工业废渣复配制备胶凝材料的实验研究

doi:10.11962/1006-4990.2020-0165

摘要/Abstract

摘要：

选择煤矸石、镁渣、粉煤灰等工业废渣作为主体原料,对原料进行粉磨筛分等处理;利用荧光分析仪和X 衍射仪检测原料的组成;设计了3组共计9个配方：煤矸石底渣+镁渣+熟料+石膏组3个、煤矸石底渣+粉煤灰+生石灰+石膏组3个、煤矸石底渣+粉煤灰+生石灰组3个;测定9个配方胶凝材料的强度、凝结时间、标准稠度、安定性等物理性能,结果表明：在生石灰、石膏双激发作用下,煤矸石灰渣、粉煤灰的水化硬化程度较高,制得的胶凝材料强度最高、28 d抗折强度可达8.2 MPa、抗压强度可达42.4 MPa。实验得到此方案的最佳配比：m（煤矸石灰渣）∶m（粉煤灰）∶m（生石灰）∶m（石膏）=15∶30∶45∶10。

关键词: 工业废渣, 活性激发, 胶凝材料

Abstract:

Clinker-lean cement was produced with coal gangue slag,magnesium slag,fly ash and other industrial residues as the main raw materials.The raw materials were ground and screened,their composition was analyzed with fluoroanalyzer and XRD,and three groups i.e.nine proportion schemes was designed as follows: three groups of coal gangue slag-magesium slag-clinker-gypsum,three groups of coal gangue slag-fly ash-lime-gypsum and three groups of coal gangue slag-fly ash-calk.The physical properties such as strength,setting time,standard consistency requiring water and stability of products of nine sche-mes were detected.The results showed that due to double activation of lime and gypsum,the degree of hydration and hardening of coal gangue slag and fly ash was higher and the strength of the prepared cementitiou product was the biggest,flexural strength and compressive strength for 28 d were 8.2 MPa and 42.4 MPa,respectively.The optimal proportion scheme after experiment was 15∶30∶45∶10（mass ratio of coal gangue ash to fly ash to lime to gypsum）.

Key words: industrial residue, reactivity activating, cementing materials

中图分类号:

TQ177.6

高建荣,李文宇,芋艳梅,刘永明. 利用多种工业废渣复配制备胶凝材料的实验研究[J]. 无机盐工业, 2021, 53(2): 77-80.

Gao Jianrong,Li Wenyu,Yu Yanmei,Liu Yongming. Experimental study on activating various industrial residues to compound and prepare cementitious materials[J]. Inorganic Chemicals Industry, 2021, 53(2): 77-80.

图/表 6

表1

图1

表2

表3

表4

表5

参考文献 18

[1]	高长明. 水泥工业低碳转型刻不容缓[J].新世纪水泥导报,2019(6):1-3.
[2]	武彦辉. 我国煤矸石的处置利用现状及展望[J].中国环保产业,2019(1):53-55.
[3]	李航宇, 阎蕊珍, 闫亚杰, 等. 粉煤灰取代水泥对再生混凝土砖性能的影响[J].新型建筑材料,2020(2):92-94,99.
[4]	郭丽娜, 赵晶, 李香平, 等. 皮江炼镁工业废渣综合利用现状与展望[J].山西冶金,2019(6):84-85
[5]	方达, 吴铭清, 邹磊, 等. 煤矸石的综合利用及其替代页岩配料生产熟料的实践[J].新世纪水泥导报,2018(1):61-64.
[6]	Yang Zhenzhou, Zhang Yingyi, Liu Lili, et al. Integrated utilization of sewage sludge and coal gangue for cement clinker products:Pro-moting tricalcium silicate formation and trace elements immobiliza-tion[J]. Materials, 2016,9(4):275. doi: 10.3390/ma9040275
[7]	曾小星. 煤矸石粉替代粉煤灰作为水泥与混凝土掺合料的试验研究[J].新型建筑材料,2015(3):12-14.
[8]	高建荣, 芋艳梅, 刘永明, 等. 镁渣高掺量配料在新型干法水泥生产中的工艺优化与技术集成[J].水泥,2019(1):24-28.
[9]	Omid Amini, Mojtaba Ghasemi. Laboratory study of the effects of us-ing magnesium slag on the geotechnical properties of cement stabili-zed soil[J]. Construction and Building Materials, 2019,223:409-420.
[10]	张祥成, 孟永彪. 浅析中国粉煤灰的综合利用现状[J]. 无机盐工业, 2020,52(2):1-2.
[11]	刘音, 王昊宇, 郭皓, 等. 大掺量粉煤灰充填材料优化配比及性能研究[J]. 矿业研究与开发, 2020,40(3):56-61.
[12]	Yang Tao, Zhang Zuhua, Zhu Huajun, et al. Re-examining the suit-ability of high magnesium nickel slag as precursors for alkali-acti-vated materials[J]. Construction and Building Materials, 2019,213:109-120.
[13]	袁宇兴, 汤裕, 郑章宏, 等. 粉煤灰-水泥基地质聚合物复合泡沫材料的研制[J]. 中国材料进展, 2018 , 37(2):134-137.
[14]	李琳, 吴红, 连明磊, 等. 高强度粉煤灰基地聚物的设计与性能研究[J]. 硅酸盐通报, 2020,39(1):183-185.
[15]	陈杰, 水中和, 孙涛, 等. 活化煤矸石在水泥基材料中的早期水化动力学研究[J]. 硅酸盐通报, 2019,38(7):1986-1990.
[16]	罗双, 付汝宾, 孔德文, 等. 掺合料对磷石膏基复合胶凝材料耐水性及强度的影响综述[J]. 无机盐工业, 2020,52(11):6-11.
[17]	华龙, 高柯, 张豪杰. 煤矸石的活性激发与应用研究[J].粉煤灰综合利用,2015(2):30-31.
[18]	Zhang Na. Effects of fly ash and slag on the properties of magnesi-um oxysulfate cement[J].Emerging Materials Research,2019(9):1-10.

材料	w（CaO）	w（SiO₂）	w（Al₂O₃）	w（Fe₂O₃）	w（SO₃）	w（MgO）	w（K₂O）	w（Na₂O）	w（TiO₂）
煤矸石灰渣	5.21	45.70	30.12	4.21	2.12	0.88	0.84	0.00	1.06
粉煤灰	32.92	33.86	20.12	1.61	3.12	3.66	0.58	0.26	0.24
镁渣	50.18	30.12	1.08	2.94	1.03	12.15	0.36	0.24	—
熟料	62.45	21.19	4.78	3.61	0.76	2.31	0.86	0.12	0.24
生石灰	93.82	3.51	2.71	0.41	0.47	—	0.12	—	0.10
石膏	37.02	2.05	0.68	0.21	48.18	0.26	0.24	—	—

组号	配方号	煤矸石灰渣	金属镁渣	粉煤灰	熟料	石灰	石膏
A	1	52	28	—	12	—	8
	2	40	40	—	12	—	8
	3	28	52	—	12	—	8
B	4	28	—	52	—	10	10
	5	14	—	46	—	30	10
	6	15	—	30	—	45	10
C	7	50	—	25	—	25	—
	8	30	—	25	—	45	—
	9	35	—	25	—	40	—

实验编号	抗折强度/MPa			抗压强度/MPa
实验编号	3 d	7 d	28 d	3 d	7 d	28 d
1	2.0	2.4	4.0	10.2	11.8	15.4
2	3.4	7.9	6.6	12.0	13.6	26.6
3	1.7	6.5	5.6	9.4	11.8	19.8

实验编号	抗折强度/MPa			抗压强度/MPa
实验编号	3 d	7 d	28 d	3 d	7 d	28 d
4	4.4	6.7	7.3	13.6	18.4	41.2
5	4.7	5.4	7.6	8.4	20.2	35.8
6	6.0	7.9	8.2	14.5	22.3	42.4
7	5.2	7.4	8.0	11.0	17.5	23.5
8	6.1	8.6	6.0	15.5	18.6	21.6
9	3.6	6.5	8.3	9.5	21.5	28.1

实验序号	标准稠度/mL	初凝时间/min	终凝时间/min	膨胀值/ mm	安定性判定
1	224	41	490	4.2	合格
2	226	46	508	3.1	合格
3	228	47	442	4.0	合格
4	218	48	440	5.4	不合格
5	216	50	444	4.8	合格
6	228	55	542	4.7	合格
7	225	50	495	2.1	合格
8	223	52	512	5.6	不合格
9	222	51	510	4.2	合格